Industrial Coatings Product Catalog | Anti‑Corrosion & Protective Coatings – HUILI
Product categories
Waterborne epoxy anti-corrosion topcoat (2K) for steel, wood, and cement surfaces.
-
Steel structures, ships, machine tools, electrical housings.
-
0.12 kg/m² at 50 µm; pot life 3 h.
-
Water-thinned 5–15%; recoat after 24 h.
Waterborne epoxy MIO intermediate coating (2K) for barrier enhancement between primer and topcoat.
-
Bridges, chemical plants, municipal and power steelwork.
-
0.15 kg/m² at 50 µm; pot life 3 h.
-
Water-thinned 5–15%; recoat 24 h–7 d.
Waterborne alkyd anti-rust coating for general steel structures and equipment.
-
Steelwork, machinery, hardware, valves, pipelines.
-
0.2 kg/m² at 50 µm; recoat ≥24 h.
-
Water-thinned ≤10%; oven drying optional.
Waterborne epoxy zinc-rich primer (2K) for cathodic protection of marine and industrial steel.
-
Ships, containers, offshore platforms, pipelines, tanks.
-
0.25 kg/m² at 50 µm; pot life 3 h.
-
Water-thinned (~5%); blast-clean to Sa 2.5.
Waterborne rust conversion primer for converting rust into a stable protective layer.
-
Tanks, bridges, pipelines, brackets, auto parts.
-
0.1 kg/m² at 40 µm; 1–2 coats.
-
Second coat within 10 min; overcoat after 24 h.
Waterborne rust-tolerant primer for steel where only partial rust removal is possible.
-
Direct-to-rust on St1–St2 prepared steel.
-
Theoretical spreading rate 0.13 kg/m² at 50 µm.
-
Water thinned 5–15%; recoat after 24 h.
Thick-film abrasion-resistant flooring coating (2K) for seamless industrial epoxy floors.
-
Workshops, warehouses, micro-control rooms and clean areas.
-
System: sealing primer, primer, mid-coat, topcoat.
-
Recommended total thickness 1.0–3.0 mm.
Solvent-resistant antistatic anti-corrosion coating (2K) for internal solvent tanks and pipelines.
-
Methanol, ethanol, benzene-series solvent tank linings.
-
Surface resistivity 10⁸–10¹¹ Ω; pot life 2 h.
-
Oil, salt spray, 5% H₂SO₄ resistance 720–1000 h.
High-pressure water jetting dedicated primer for maintenance on damp steel.
-
Tanks, bridges, pipelines, gas holders, equipment repairs.
-
Water-thinned <5%; recoat after ≥2 h.
-
Surface dry 30 min; 40 µm DFT at 0.1 kg/m².
Cold spray zinc anti-corrosion primer for replacing hot-dip or thermal-sprayed zinc.
-
Towers, bridges, pipelines, tanks, containers, ships.
-
Total zinc content 96%; surface dry 20 min.
-
Single-component; recoat after ≥10 h.
Chlorinated ether anti-corrosion coating for steelwork and concrete equipment.
-
Ships, containers, port machinery, bridges, gas holders.
-
Single-pack; recoat interval ≥12 h.
-
Weathering, seawater, and chemical resistance.
Epoxy furan glass flake coating (2K) for wet-service heavy-duty corrosion protection.
-
Underwater/humid areas and heavy chemical zones.
-
Mix ratio 20:4; pot life 4 h.
-
Salt water resistance: 1 year unchanged.
Anti-mildew coating for interior workshop walls in food and beverage plants.
-
Beer, dairy, beverage, bakery, pharmaceutical workshops.
-
2–4 coats; recoat interval 4–6 h.
-
10% NaOH 240 h; 5% H2SO4 72 h.
Epoxy phenolic coating (2K) for tanks and steel in chemical service.
-
Chemical media tanks and equipment.
-
Mix ratio 24:3; pot life 3 h.
-
Resists acids/alkalis/salts; seawater resistance.
Polysiloxane topcoat (2K) for steelwork in severe atmospheric corrosion.
-
Petrochemical, power, pipelines, tanks, gas holders.
-
Mix ratio 24:3; pot life 4 h.
-
High weathering; anti-chalking, anti-yellowing.