CSPE cooling tower damp-proof coating for inner wall anti-corrosion service.
For cooling tower inner wall protection.
Single-component; min recoat 12 h at 25°C.
Resists freeze-thaw, damp heat, and mildew.
Polyurethane cooling tower damp-proof coating (2K) for waterproof anti-corrosion lining.
For cooling towers, sewage tanks, mines, underground buildings.
Primer ratio 24:3; topcoat ratio 18:3.
Pot life 4 h; min recoat 12 h.
Premium polyurethane marking coating (2K) for steel structures and concrete chimneys.
For chimney marking and protection.
Mixing ratio 18:3; pot life 4 h.
High gloss; fully hardened 7 d at 25°C.
Epoxy bitumen cooling tower damp-proof coating (2K) for cooling tower inner wall protection.
For cooling towers, sewage tanks, underground mines.
Mixing ratio 25:2.5; pot life 4 h.
Waterproof, anti-seepage, and mildew resistant.
Chlorinated rubber acrylic marking coating for chimneys and steel tower marking.
For power plant concrete chimneys and steel towers.
Single-component; min recoat 12 h at 25°C.
Gloss ≥70; 25°C surface dry 1 h.
Premium acrylic marking coating for chimney and steel tower marking.
For power plant concrete chimneys and steel towers.
Single-component; min recoat 12 h at 25°C.
Thinner X-14; dilution 3–7%.
Long-lasting special marking coating for chimney and tower marking/protection.
For steel structures and concrete chimneys.
Single-component; min recoat 24 h at 25°C.
Gloss ≥80; dry to touch 1 h.
Perchloroethylene enamel for mechanical equipment and metal parts finishing.
For protective and decorative finishing on metals.
Single-component; min recoat 12 h at 25°C.
Thinner X-1; dilution 3–7%.
Perchloroethylene anti-corrosion coating for equipment, metal structures, and concrete.
For mechanical equipment, metal structures, concrete surfaces.
Single-component; min recoat 12 h at 25°C.
Primer/topcoat system available under PLG52.
Chlorosulfonated polyethylene gas holder dedicated coating for gas holder outer wall protection.
For gas holders; also for other steel structures.
Single-component; min recoat 24 h at 25°C.
Resists water, H₂S, and chemical gas corrosion.
Chlorosulfonated polyethylene topcoat for chemical-atmosphere steel and concrete protection.
For corrosive environments on steel and concrete.
Single-pack; min recoat 24 h at 25°C.
Thinner X-1; dilution 3–7%.
Chlorosulfonated polyethylene anti-rust coating for metal structures and concrete anti-corrosion.
For metal structures, equipment, concrete surfaces.
Single-pack; min recoat 10 h at 25°C.
Topcoat compatible with CSPE and H-CPE systems.
High-chlorinated polyethylene topcoat for steel and concrete anti-corrosion finishing.
For steel structures and concrete surfaces.
Single-pack; recoat 24 h to 7 d at 25°C.
Thinner X-16; dilution 3–7%.
High-chlorinated polyethylene enamel for chemical-industry steel and concrete finishing.
For chemical, petroleum, metallurgy, power industries.
Silver white: split-pack; mixing ratio 6:1.
Thinner X-16; dilution 3–7%.
High-chlorinated polyethylene intermediate coating for corrosion resistance and “three-proof” service.
Intermediate layer; can be used as first coat.
Single-pack; min recoat 12 h at 25°C.
Compatible with acrylic and chlorinated ether topcoats.
High-chlorinated polyethylene anti-rust coating for steel and concrete in corrosive atmospheres.
For chemical-atmosphere and industrial-atmosphere corrosion.
Single-pack; thinner X-16 at 3–7%.
Compatible with high-chlorinated polyethylene topcoats.
Chlorinated rubber acrylic anti-corrosion topcoat for equipment and industrial building surfaces.
For harsh-environment surface protection and finishing.
Single-pack; min recoat 12 h at 25°C.
Compatible over epoxy and chlorinated rubber primers.
Chlorinated rubber red iron oxide anti-rust coating for steel structure protection.
For steel structures anti-rust and anti-corrosion.
Single-pack; min recoat 12 h at 25°C.
Compatible with chlorinated rubber and acrylic topcoats.