Industrial Coatings & Anti-Corrosion Systems | Product Catalog – HUILI
Waterborne rust-tolerant primer for steel where only partial rust removal is possible.
Direct-to-rust on St1–St2 prepared steel.
Theoretical spreading rate 0.13 kg/m² at 50 µm.
Water thinned 5–15%; recoat after 24 h.
Waterborne rust conversion primer for converting rust into a stable protective layer.
Tanks, bridges, pipelines, brackets, auto parts.
0.1 kg/m² at 40 µm; 1–2 coats.
Second coat within 10 min; overcoat after 24 h.
Waterborne epoxy zinc-rich primer (2K) for cathodic protection of marine and industrial steel.
Ships, containers, offshore platforms, pipelines, tanks.
0.25 kg/m² at 50 µm; pot life 3 h.
Water-thinned (~5%); blast-clean to Sa 2.5.
Waterborne alkyd anti-rust coating for general steel structures and equipment.
Steelwork, machinery, hardware, valves, pipelines.
0.2 kg/m² at 50 µm; recoat ≥24 h.
Water-thinned ≤10%; oven drying optional.
Waterborne epoxy MIO intermediate coating (2K) for barrier enhancement between primer and topcoat.
Bridges, chemical plants, municipal and power steelwork.
0.15 kg/m² at 50 µm; pot life 3 h.
Water-thinned 5–15%; recoat 24 h–7 d.
Waterborne epoxy anti-corrosion topcoat (2K) for steel, wood, and cement surfaces.
Steel structures, ships, machine tools, electrical housings.
0.12 kg/m² at 50 µm; pot life 3 h.
Water-thinned 5–15%; recoat after 24 h.
Waterborne acrylic anti-corrosion topcoat for indoor/outdoor steel and chassis components.
Automotive chassis, locomotives, steel structures, guardrails.
0.14 kg/m² at 50 µm; recoat ≥24 h.
Water-thinned 10–25%; blast or power-tool clean.
Waterborne acrylic amino baking coating for decorative protection of small metal parts.
Bicycles, e-bikes, appliances, instrument housings.
0.1 kg/m² at 25 µm; bake 130℃×30 min.
Water-thinned 10–50%; flash-off 10–15 min.
Waterborne acrylic amino silver baking coating for metallic decorative protection on small parts.
Bicycle, e-bike, and appliance metal components.
0.1 kg/m² at 30 µm; bake 130℃×30 min.
Water-thinned 5–15%; silver metallic appearance.
Waterborne amino baking coating for economical protection of bicycle and appliance parts.
Bicycles, e-bikes, home appliance metal parts.
0.1 kg/m² at 25 µm; bake 120–130℃×30 min.
Water-thinned 20–50%; flash-off 10–15 min.
Waterborne fluorocarbon coating for durable exterior walls and roofs.
Exterior concrete, building panels and roofs.
0.15 kg/m² at 50 µm; recoat ≥2 h.
Water-thinned 5–10%; use suitable primer system.
Waterborne anti-mold coating for walls in food and beverage plants.
Breweries, bakeries, dairy and soy-product workshops.
0.13 kg/m² at 50 µm; recoat 24–168 h.
Water-thinned 5–10%; requires full mold removal.
Waterborne epoxy antistatic coating (2K) for hydrocarbon tank internals.
Crude oil, gasoline, kerosene and diesel tanks.
0.11 kg/m² at 40 µm; pot life 2 h.
Water-thinned 5–15%; blast to Sa 2.5.
Waterborne dip-coating system for frames, chassis and small metal parts.
Transport frames, farm machinery and hardware pieces.
0.05–0.11 kg/m² at 25 µm DFT.
Dip-application; water-thinned to line viscosity.
Waterborne alkyd general-purpose coating for indoor/outdoor metal and wood.
General metalwork and wood components.
0.15 kg/m² at 50 µm; recoat ≥24 h.
Water thinning ≤10%; optional 90℃ oven dry.
Waterborne fluorocarbon protective coating (2K) for exposed steel structures.
Bridges, towers, large gates, chemical equipment.
0.16 kg/m² at 50 µm; pot life 3 h.
Water-thinned 5–10%; apply over blasted steel.
Protect. Perform. Endure. – Advanced Coatings for Industrial Excellence.