PLH-1 Thick-Film Abrasion-Resistant Flooring Coating

Overview
Two-component epoxy-based thick-film flooring coating for hard-wearing, seamless, decorative industrial floors.​

Composition
Selected epoxy resin with imported curing agent, pigments, and multiple additives; supplied as Part A & Part B.​

Typical uses
Floor protection and decoration for workshops, warehouses, and control rooms in pharmaceutical, chemical, food processing, electronics, light industry, machinery, and automobile manufacturing.​

Technical data (typical)

• Recommended total film thickness: 1.0–3.0 mm, depending on compressive strength and load requirements.​

Application data (25°C)

• Process sequence: surface preparation → sealing primer → primer → mid-coat → sanding and dust removal → topcoat.​

• Recoat intervals: 10–20°C, min 24 h; 20–30°C, min 12 h; max 7 d.​

• Application methods: sealing primer by spray/brush; primer and mid-coat by trowel; topcoat preferably by spray.​

• Mixing ratio: sealing primer/primer/mid-coat A:B = 1.5:1; topcoat A:B = 3:1.​

• Mixing notes: Part A is coating liquid; Part B is universal hardener; add graded abrasion-resistant aggregate into mixed primer/mid-coat and stir mechanically; use within 4 h.​

Surface preparation

• Cement substrate mechanically trowelled and finished with cement mortar; compressive strength meeting design; no cement powder dusting on surface; surface flat.​

• New substrate curing period ≥30 d.​

System compatibility / packing / storage

• Construction conditions: do not apply below 5°C or above 85% RH; choose winter-type flooring coating in low temperature; no follow-up works allowed on finished flooring; cure 7 d before service.​

• Storage: dry, cool, ventilated; away from fire; avoid strong sunlight; no outdoor storage.​

• Shelf life: 12 months.