Industrial Coatings & Anti-Corrosion Systems | Product Catalog – HUILI
Special Epoxy Primer (2K) – Two-component special epoxy primer for industrial corrosion protection.
For power, bridge, petrochemical, marine, and port facilities/equipment.
Pot life 2 h (25°C); mix ratio 25:2.5.
Compatible with epoxy MIO intermediate and epoxy/PU topcoat systems.
Epoxy heavy-duty anti-corrosion coating (2K) for tank linings and severe chemical service.
Tanks/vessels for oils and aromatic solvents.
Pot life 2 h; recoat 24 h–7 d.
Resists acids, alkalis, salts, oils, benzene solvents.
Epoxy topcoat (2K) for steel and concrete in industrial and marine facilities.
Water treatment, ports, sluice gates, workshops.
Mix ratio 20:4; recoat 24 h–7 d.
Water, oil, humid-heat, chemical resistance; impact resistant.
Solvent-free epoxy coating (2K) for thick-film protection on steel and tanks.
Steel structures and storage tank surfaces.
Pot life 45 min; up to 400 µm/coat.
100% solids; oil, water, solvent resistance.
Modified epoxy weather-resistant topcoat (2K) for outdoor corrosion protection.
Ports, pipelines, offshore, ships, sluice gates.
Mix ratio 20:5; recoat 16 h–7 d.
Acid/alkali/salt resistance; color and gloss retention.
Epoxy Zinc-Rich Primer (2K) – Two-component epoxy zinc-rich primer for steel anti-corrosion systems.
For shipbuilding/repair, bridges, towers, gas holders, oil tanks, and steel structures.
Water and oil resistance with excellent adhesion.
Theoretical consumption 0.21 kg/m² at approx. 50 µm DFT (losses not included).
High-Grade Epoxy Enamel (2K) – Epoxy enamel for decorative heavy-duty corrosion protection.
For steel structures and concrete surfaces.
Mix ratio 20:4; pot life 4 h.
Recoat 12 h–7 d; X-7 thinner 2–8%.
Epoxy High-Build Topcoat (2K) – High-solids epoxy topcoat for heavy-duty protection.
For steel structures and concrete surfaces.
Induction time 5 h; pot life 3 h.
Recoat 24 h–7 d; X-7 thinner 3–9%.
Epoxy Glass Flake Topcoat (2K) – Epoxy glass flake topcoat for wet or chemical zones.
For underwater/humid areas and heavy chemical plants.
Mix ratio 20:2; pot life 4 h.
Salt water resistance: 1 year, no change.
Epoxy Aluminium Pigmented Topcoat (2K) – High-build epoxy topcoat with aluminium paste.
For tanks, pipelines, and steel structures.
Mix ratio 24:4; pot life 4 h.
High solids; thick film reduces coat numbers.
Solvent-free epoxy ceramic coating (2K) for thick-film protection on tanks and pipelines.
Pipelines, chemical equipment, tank surfaces.
Pot life 4 h; recoat 24 h–7 d.
98% solids; smooth, hard, chemical resistant.
Epoxy Red Lead Anti-Rust Primer (2K) – Two-component epoxy anti-rust primer for steel corrosion protection.
Epoxy MIO intermediate coating (2K) for barrier protection in cathodic-protection coating systems.
Used with PLH53-35 epoxy zinc primer as a supporting intermediate coat.
Salt water resistance: 20 days (as stated).
Mixing ratio 8:1 (by weight); recommended DFT 60–90 µm per coat.
Epoxy Iron Oxide Red Anti-Rust Primer (2K) – Two-component epoxy anti-rust primer for steel structures.
For general steel structure corrosion protection; can be used for concrete with an epoxy sealer primer.
Mix ratio 24:3; pot life 4 h (25°C).
Recoat 24 h–7 d (25°C); overcoatable with epoxy and polyurethane systems.
Epoxy MIO Intermediate Coating (2K) – Two-component epoxy micaceous iron oxide intermediate coating for barrier protection.
For ships, containers, bridges, steel gates, gas holders, port machinery, and steel structures; used over zinc-rich primer or sprayed zinc.
Mix ratio 27:3; pot life 4 h (25°C).
Recoat 12 h–7 d (25°C); overcoatable with epoxy and polyurethane systems.
Epoxy Zinc Primer (2K, C6-Modified) – Two-component epoxy zinc primer (C6-modified) for cathodic-protection priming.
Salt spray resistance 1300 h (as stated).
Theoretical consumption 0.25 kg/m² at 50 µm DFT (losses not included).
For offshore platforms, underwater steel, pipelines, oil tanks, bridges, and petrochemical steel structures.