PLSX-06 Waterborne Epoxy MIO Intermediate Coating

Overview
Two-component waterborne epoxy micaceous iron oxide intermediate coating for enhanced barrier protection between primer and topcoat.​

Composition
Waterborne epoxy resin dispersion and curing agent with micaceous iron oxide, anti-rust pigments, functional fillers, and additives; supplied as Part A & Part B.​

Typical uses
Intermediate layer between primer and topcoat to increase total film thickness and improve barrier properties for heavy-duty protection of steel and concrete in bridges, chemical plants, transport, municipal, and power industries.​

Technical data (typical)

• Appearance: grey or brown.​

• Density: 1.6 kg/L.​

• Theoretical consumption: 0.15 kg/m² at 50 µm DFT (loss not included).​

• Drying time (25°C): surface dry 1 h; hard dry 24 h; full dry 7 d.​

Application data (25°C)

• Application methods: spray, brush, roller.​

• Pot life: 3 h.​

• Thinner: clean water, recommended 5–15%.​

• Recoat interval: min 24 h; max 7 d.​

Surface preparation
When applied over two-component primers: surfaces must be clean, dry, and free of contamination; if exceeding maximum recoat interval, pre-coat must be roughened.​
When used as first primer: blast to Sa 2.5 or power-tool clean to St 3 with 30–75 µm profile.​

System compatibility / packing / storage

• Construction conditions: ambient 5–35°C and at least 3°C above dew point; not suitable in rain, fog, snow, or RH ≥85%.​

• Storage: dry, cool, ventilated; 5–35°C; avoid strong sunlight; no outdoor storage.​

• Shelf life: 6 months.