Non-toxic epoxy coating (2K) for water-contact linings and sanitary storage spaces.
Tap-water pipelines, water tanks, grain silos.
Pot life 4 h; thinner 3–8%.
Non-benzene solvent; low odor during application.
Overview
Two-component epoxy coating system (primer/topcoat) formulated for internal lining protection where low odor and non-benzene solvent formulation is required.
Composition
Imported special epoxy resin, curing agent, medical-grade pigments, fillers, additives; supplied as two components for both primer and topcoat.
Typical uses
Internal lining protection for tap-water pipelines, water storage tanks, drinking water tanks/compartments, fresh water tanks, dry cargo holds, and grain silos.
Protection for steel or concrete equipment/facilities in medical, food, beer, and beverage industries.
Technical data (typical)
Appearance: primer iron red; topcoat white.
Theoretical consumption: primer 0.2 kg/m² at 60 µm DFT (loss not included).
Theoretical consumption: topcoat 0.2 kg/m² at 60 µm DFT (loss not included).
Density: primer 1.3 kg/L; topcoat 1.25 kg/L.
Drying time (25°C): surface dry 2 h; hard dry 24 h; full cure 7 d.
Application data (25°C)
Mixing ratio (A:B): primer 20:4.8; topcoat 20:7.5.
Induction time: 5 min.
Pot life: 4 h.
Application methods: airless spray, brush, roller.
Thinner: H55-28 dedicated thinner, 3–8%.
Recoat interval: min 24 h; max 7 d.
Recommended DFT per coat: 60–80 µm (roller 40–50 µm).
System: non-toxic epoxy primer + non-toxic epoxy topcoat.
Surface preparation
Steel: blast to Sa 2.5 or power-tool clean to St 3; surface profile 30–75 µm.
Concrete: dry, sound, free of alkali/oil/sand; apply sealer primer, then apply primer and putty for leveling.
System compatibility / packing / storage
System compatibility: non-toxic epoxy primer + non-toxic epoxy topcoat.
Packing: primer Part A 20 kg, Part B 4.8 kg; topcoat Part A 20 kg, Part B 7.5 kg.
Storage: dry, cool, ventilated; away from fire; avoid strong sunlight; no outdoor storage.
Shelf life: 12 months.
We would love to speak with you.
Feel free to reach out using the below details.
Modified Epoxy Iron Oxide Red Primer (2K) – Two-component modified epoxy iron oxide red anti-rust primer for steel and concrete.
For corrosion protection of steel structures and concrete surfaces.
Water and corrosion resistance with strong adhesion (as described).
Mix ratio 24:3; recoat 24 h–7 d (25°C).
Epoxy zinc phosphate anti-rust primer (2K) for heavy-duty steel corrosion protection.
For ports/docks, heavy structures, mining machinery, power machinery plants, and water conservancy steelwork.
Zinc phosphate anti-rust pigment system with stated water and salt water resistance.
Mix ratio 7:1; theoretical consumption 0.12 kg/m² at 50 µm DFT.
Epoxy ester anti-rust primer for steel structures (single-pack).
For guardrails and mining/mineshaft equipment steel surfaces.
Air-drying or low-temperature baking curing is specified.
Single-pack with no pot life limit (as stated); compatible with alkyd topcoats/enamels.
Epoxy MIO Intermediate Coating (2K) – Two-component epoxy micaceous iron oxide intermediate coating for barrier protection.
For ships, containers, bridges, steel gates, gas holders, port machinery, and steel structures; used over zinc-rich primer or sprayed zinc.
Mix ratio 27:3; pot life 4 h (25°C).
Recoat 12 h–7 d (25°C); overcoatable with epoxy and polyurethane systems.