Winter-grade epoxy coal tar bitumen coating (2K) that can be applied at -5°C.
Buried pipelines; steel and concrete protection.
Mix ratio 20:4; recoat 12 h–7 d.
Seawater, oil, chemical resistance; high insulation.
PLHL52-3 Winter-Grade Epoxy Coal Tar Bitumen Coating is a two-component winter-grade epoxy coal tar bitumen coating designed to cure under low-temperature conditions. This coating is used for corrosion protection of steel and concrete in severe corrosive environments and is suitable for the external anti-corrosion of buried pipelines.
It is composed of epoxy resin, coal tar pitch, anti-rust pigments, solvent, additives, catalyst, and a fast-drying curing agent, and is supplied as Part A and Part B.
Designed to cure under low-temperature conditions.
Suitable for corrosion protection of steel and concrete.
Suitable for severe corrosive environments.
Suitable for external anti-corrosion of buried pipelines.
Volume solids: ≥75%.
This coating is suitable for a wide range of steel and concrete protection projects in industrial environments.
Steel structures in severe corrosive environments
Concrete structures in severe corrosive environments
External anti-corrosion of buried pipelines
Blast to Sa 2.5 or power-tool clean to St 3; surface profile 30–75 µm.
Storage
store in a dry, cool, ventilated place; keep away from fire; avoid strong sunlight; no outdoor storage.
System compatibility: winter-grade epoxy coal tar bitumen primer + winter-grade epoxy coal tar bitumen topcoat.
This product is a two-component winter-grade epoxy coal tar bitumen coating supplied as Part A and Part B.
This coating is used for steel and concrete.
This coating is used for corrosion protection in severe corrosive environments and for the external anti-corrosion of buried pipelines.
This coating can be applied by spray, brush, or roller.
HL52-6 dedicated thinner should be used, with 3–8% dilution.
The recommended dry film thickness per coat is 40–70 µm, or 30–40 µm by brush/roller.
We would love to speak with you.
Feel free to reach out using the below details.
Indoor Non-Intumescent Fireproof Coating for Steel Structure – Indoor cementitious thermal-insulation fireproof coating for steel.
3 h rating: ≥33 mm; 20–22 kg/m²; 5–6 coats.
Air spray 0.6–0.8 MPa; nozzle Φ4.0–6.0 mm.
Fire test: 32 mm thickness; 5400 mm span; 3.00 h.
Vinyl Phosphating Primer (2K) – Two-component phosphating primer for galvanized steel, aluminum, and other light metals.
Forms chemical adhesion to improve intercoat adhesion of subsequent coatings.
Low film thickness system: 15–25 µm DFT per coat; theoretical consumption 0.06 kg/m² at 20 µm DFT.
Min. recoat 2 h (25°C); dedicated PLX06 thinner (10–20%).
Inorganic Zinc Silicate Primer (2K) – Two-component inorganic zinc silicate primer for long-term steel corrosion protection with cathodic protection.
For blast-cleaned steel; surface preparation Sa 3 (not lower than Sa 2.5) is specified.
Fast drying at 25°C, RH 70–85%: touch dry 10 min; hard dry 2 h; cured 24 h.
Mix ratio 28:7; thinner X-11 inorganic zinc thinner (5–20%); compatible with epoxy/PU coating systems.
Epoxy Iron Oxide Red Anti-Rust Primer (2K) – Two-component epoxy anti-rust primer for steel structures.
For general steel structure corrosion protection; can be used for concrete with an epoxy sealer primer.
Mix ratio 24:3; pot life 4 h (25°C).
Recoat 24 h–7 d (25°C); overcoatable with epoxy and polyurethane systems.
Protect. Perform. Endure. – Advanced Coatings for Industrial Excellence.
© 2025 All Rights reserved Anhui HUILI Coating Technology Co., Ltd. | Privacy Policy