Overview
Two-component epoxy glass flake anti-rust intermediate coating with barrier performance, waterproofing/anti-permeation properties, and chemical resistance.​
It is described as having strong adhesion, a tough and wear-resistant film, high mechanical strength, and long-term corrosion protection.​

Composition
Epoxy resin, glass flakes, anti-rust pigments, additives, solvent, and curing agent; supplied as Part A and Part B.​

Typical uses

• Anti-rust and anti-corrosion protection for steel and concrete substrates in ship, offshore engineering, underground mines, chemical areas, wastewater treatment and other heavy-duty corrosion environments.​

Technical data (typical)

• Appearance / color: Iron oxide red, light gray, white.​

• Theoretical consumption: 0.12 kg/m² at 50 µm DFT (losses not included).​

• Density / specific gravity: 13 kg/L.​

• Drying / curing (25°C): Touch dry 1 h; hard dry 24 h; full cure 7 days.​

Application data (25°C)

• Mixing ratio (A:B): 25:2.5.​

• Induction time: 5 min.​

• Pot life: 4 h.​

• Application methods: Airless spray, brush, roller.​

• Thinner / Cleaner: X-7 epoxy thinner; typical dilution 2–8% (air spray/roller may require more).​

• Recoat interval / overcoating interval (25°C): Minimum 24 h; maximum 7 days.​

• Recommended DFT: 60–80 µm per coat (brush/roller: 30–50 µm per coat).​

Surface preparation

• Abrasive blasting or shot blasting to Sa 2.5, or power-tool cleaning to St 3; surface profile 30–75 µm.​

System compatibility / packing / storage

• Compatible system: epoxy glass flake anti-rust intermediate coating and topcoat (as stated).​

• Shelf life: 12 months.​

• Storage: Store in a dry, cool, ventilated warehouse away from fire sources and direct sunlight; outdoor storage is not permitted.​

• Packaging: Part A 25 kg; Part B 2.5 kg.