Solvent-free epoxy coating (2K) for thick-film protection on steel and tanks.
Steel structures and storage tank surfaces.
Pot life 45 min; up to 400 µm/coat.
100% solids; oil, water, solvent resistance.
PLH-50 Solvent-Free Epoxy Coating is a two-component solvent-free epoxy coating for high-build anti-corrosion protection. This coating is used for anti-corrosion protection on steel structures and storage tank surfaces with high requirements.
It is composed of epoxy resin, modified curing agent, special pigments and fillers, and additives, and is supplied as Part A and Part B.
Designed for high-build anti-corrosion protection.
Suitable for steel structures and storage tank surfaces.
Solvent-free formulation.
Volume solids: 100%.
Can be used at 70–150 µm per coat.
Can be applied up to 400 µm with special equipment.
This coating is suitable for a wide range of steel protection projects in industrial environments.
Steel structures
Storage tank surfaces
Anti-corrosion projects with high-build coating requirements
Blast to Sa 2.5 or power-tool clean to St 3; surface profile 30–75 µm.
Storage
dry, cool, ventilated; away from fire; avoid strong sunlight; no outdoor storage.
System compatibility: generally self-priming / self-finishing.
This product is a two-component solvent-free epoxy coating supplied as Part A and Part B.
This coating is used for steel structures and storage tank surfaces.
The volume solids content is 100%.
This coating can be applied by airless spray or brush.
X-7 epoxy thinner may be used; minimize thinning or do not thin.
The recommended dry film thickness per coat is 70–150 µm, and it can be applied up to 400 µm with special equipment.
We would love to speak with you.
Feel free to reach out using the below details.
Special Outdoor Non-Intumescent Fireproof Coating for Steel Structure – Special cementitious coating for hydrocarbon-flame fire protection.
For petrochemical/chemical outdoor steel structures.
3 h rating: ≥33 mm; 20–22 kg/m²; 5–6 coats.
Air spray 0.6–0.8 MPa; nozzle Φ4.0–6.0 mm.
Outdoor Non-Intumescent Fireproof Coating for Steel Structure – Outdoor non-intumescent fireproof coating for steel structures.
3 h rating: ≥33 mm; 20–22 kg/m²; 5–6 coats.
Bond strength test result: 0.11 MPa.
Fire test: 33 mm thickness; 5400 mm span; 3.00 h.
Outdoor Intumescent Fireproof Coating for Steel Structure – Waterborne intumescent coating for outdoor steel fire protection.
2 h rating: ≥3.2 mm; 4.5 kg/m² theoretical consumption.
Air spray 0.6–0.8 MPa; nozzle Φ4.0–6.0 mm.
Bond strength test result: 0.77 MPa.
Inorganic Zinc-Rich Primer (2K) – Two-component ethyl silicate zinc-rich primer for cathodic protection of blast-cleaned steel.
General-purpose use for bridges, towers, gas holders, oil tanks, oil/gas pipelines, and industrial steel structures.
High zinc dust content with stated water/oil/media resistance and welding/cutting resistance.
Sa 3 surface preparation (not lower than Sa 2.5); touch dry 10 min at 25°C, RH 70–85%.