SPUA Polyurea Anti-Corrosion Material

100% solids polyurea anti-corrosive coating with rapid on-site cure, seamless pinhole-free film and zero VOC for chemical, marine, waterproofing and abrasion-resistant industrial applications. Excellent adhesion to steel, aluminum and concrete substrates.

SPUA Polyurea Anti-Corrosion Material Description

Overview
Fast-curing polyurea anti-corrosion material for protective coating applications requiring rapid build and seamless film.

Composition

Typical uses
Used in chemical anti-corrosion engineering, waterproof protection engineering, wear-resistant engineering, sports engineering, military engineering, marine engineering, and power engineering.

Technical data (typical)

Corrosion resistance medium	Result
Saturated brine	Good
Ammonium nitrate	Good
Sodium chloride	Good
Sodium phosphate	Good
Sodium perchlorate	Good
Acetic acid (100%)	Good
Hydrochloric acid (5%, 10%)	Good
Nitric acid (20%)	Discoloration and embrittlement
Sulfuric acid (5%, 10%, 20%)	Good
Sulfuric acid (50%)	Discoloration and embrittlement
Phosphoric acid (10%)	Good
Phosphoric acid (50%)	Discoloration and embrittlement
Hydrofluoric acid	Discoloration and embrittlement
Sodium hydroxide / potassium hydroxide (10%)	Good
Ammonia water (20%)	Good
Gasoline / diesel / mineral oil	Good
Benzene / toluene	Discoloration and blistering

Contact Us

We would love to speak with you.
Feel free to reach out using the below details.

PLH52-1 High-Grade Epoxy Enamel

2K epoxy enamel with a porcelain-smooth, abrasion-resistant film for decorative heavy-duty corrosion protection on steel and concrete. Chemical, oil and moisture resistant. 30µm DFT per coat, 3-coat system to 100µm.

GT-NSF-Fp3.00 Indoor Non-Intumescent Fireproof Coating for Steel Structure

Cementitious non-intumescent fire-resistant coating with 3-hour fire rating for indoor steel structures including stations, warehouses and stadiums. Non-corrosive to steel, smoke-free and non-toxic. Sa2.5 prep, 16–32mm total application thickness.

PLE06-4 Inorganic Zinc-Rich Primer

2K ethyl silicate inorganic zinc-rich primer with high zinc content for maximum cathodic protection on industrial steel. Engineered for bridges, transmission towers & oil pipelines. Weld and cut tolerant, Sa2.5 prep, 40–80µm DFT.