Acrylic high-build topcoat for steel, concrete, and above-waterline ship areas.
For steel structures, concrete, and building walls.
Single-pack; min recoat 12 h at 25°C.
Thinner X-14; dilution 3–7%.
Overview
Single-pack acrylic high-build topcoat with good abrasion and impact resistance.
Provides resistance to seawater, mineral oil, and animal/vegetable oils, with weathering, color retention, and gloss retention.
Composition
Formulated with acrylic resin, plasticizer, weather-resistant pigments, fillers, additives, and solvents.
Typical uses
Protective topcoat for steel structures and concrete.
Also suitable for ship topside and above-waterline areas, and as protective/decorative finishing for building walls.
Technical data (typical)
Appearance: Various colors.
Theoretical consumption: 0.24 kg/m² at 60 μm DFT (excluding loss).
Density: 1.2 kg/L.
Solids: 80% (by weight); 65% (by volume).
Drying time (25°C): Surface dry 0.5 h; hard dry 2 h.
Application data (25°C)
Mixing: Single-pack.
Induction time: None.
Pot life: Unlimited.
Application methods: Airless spray, brush, roller.
Thinner: X-14 acrylic thinner; dilution 3–7%.
Recoat interval (25°C): Min 12 h; max unlimited.
Recommended coats / DFT: 1 coat 30–60 μm; brush/roller 1 coat 30–40 μm.
Surface preparation
Remove dust and oil contamination from the previous coat; if beyond maximum recoat interval, consider roughening as needed.
When used as the first coat: blast/shot blast to Sa 2.5 or power-tool cleaning to St 3; surface profile 30–75 μm.
System compatibility / packing / storage
Compatibility: Previous coat—epoxy primer; epoxy intermediate coating; chlorinated rubber anti-rust coating; acrylic anti-rust coating.
Packing: 22 kg.
Storage: Shelf life 12 months; store dry/cool/ventilated, away from fire and direct sunlight; no outdoor stacking.
We would love to speak with you.
Feel free to reach out using the below details.
Inorganic Zinc Silicate Primer (2K) – Two-component inorganic zinc silicate primer for long-term steel corrosion protection with cathodic protection.
For blast-cleaned steel; surface preparation Sa 3 (not lower than Sa 2.5) is specified.
Fast drying at 25°C, RH 70–85%: touch dry 10 min; hard dry 2 h; cured 24 h.
Mix ratio 28:7; thinner X-11 inorganic zinc thinner (5–20%); compatible with epoxy/PU coating systems.
Epoxy Sealer Primer (2K) – Two-component penetrating sealer primer for porous substrates.
For cement mortar, concrete, and fiber cement boards; also stated for wood.
Concrete moisture content < 6% before application (as stated).
Mix ratio 16:4; theoretical consumption 0.29 kg/m² at 50 µm DFT.
Modified Epoxy Iron Oxide Red Primer (2K) – Two-component modified epoxy iron oxide red anti-rust primer for steel and concrete.
For corrosion protection of steel structures and concrete surfaces.
Water and corrosion resistance with strong adhesion (as described).
Mix ratio 24:3; recoat 24 h–7 d (25°C).
Epoxy MIO Intermediate Coating (2K) – Two-component epoxy micaceous iron oxide intermediate coating for barrier protection.
For ships, containers, bridges, steel gates, gas holders, port machinery, and steel structures; used over zinc-rich primer or sprayed zinc.
Mix ratio 27:3; pot life 4 h (25°C).
Recoat 12 h–7 d (25°C); overcoatable with epoxy and polyurethane systems.