2K epoxy coating system covering primer and topcoat for petroleum product tank interiors including aviation fuel, diesel and lubricant oil service. Non-toxic, abrasion-resistant film. Sa2.5 prep, 150–200µm total DFT system.
Overview
Two-component epoxy tank internal lining coating (primer/topcoat) for refined oil storage compartments and tanks.
Composition
Epoxy resin, corrosion-resistant pigments and fillers, blended solvent, additives, modified amine curing agent; supplied as Part A & Part B.
Typical uses
Internal lining anti-corrosion for compartments and storage tanks for gasoline, diesel, kerosene, and engine oil.
For steel storage tanks holding multiple products where static accumulation may occur.
Technical data (typical)
Appearance: primer iron red or grey; topcoat grey.
Theoretical consumption: 0.24 kg/m² at 100 µm DFT (loss not included).
Density: 1.4 kg/L.
Drying time (25°C): surface dry 2 h; hard dry 24 h; full cure 7 d.
Application data (25°C)
Mixing ratio (A:B): primer 20:2.5; topcoat 20:3.
Induction time: 5 min.
Pot life: 2 h.
Application methods: airless spray, brush, roller.
Thinner: X-7 epoxy thinner, 3–9%.
Recoat interval: min 24 h; max 7 d.
Recommended DFT per coat: 70–100 µm (brush/roller 30–50 µm).
System: PLH54-2 primer + topcoat.
Surface preparation
After compartment/tank assembly, abrasive blast clean to Sa 2.5; surface profile 30–75 µm.
If an inorganic zinc silicate shop primer is used for temporary protection, check curing; if under-cured, re-blast to remove it and clean contaminants before coating.
System compatibility / packing / storage
System compatibility: PLH54-2 refined oil tank internal lining primer + topcoat.
Packing: primer Part A 20 kg, Part B 2.5 kg; topcoat Part A 20 kg, Part B 3 kg.
Storage: dry, cool, ventilated; away from fire; avoid strong sunlight; no outdoor storage.
Shelf life: 12 months.
We would love to speak with you.
Feel free to reach out using the below details.
Single-component water-based intumescent coating delivering a 2-hour fire rating for indoor steel structures and building frames. Non-toxic, low-VOC formulation with strong adhesion. Sa2.5 prep required, 1.7–3.3mm application thickness.
2K epoxy sealer primer engineered for deep penetration and encapsulation of concrete and cement substrates. Seals and stabilizes surfaces to optimize adhesion for subsequent coating systems. Surface dry in 1 hour, full cure in 7 days.
2K epoxy zinc phosphate primer with outstanding saltwater resistance and adhesion for heavy industrial applications. Engineered for port facilities, mining equipment & hydraulic steel in aggressive environments. Sa2.5 prep required, iron red or gray finish.