Single-component chlorinated rubber topcoat with excellent weathering, seawater and chemical resistance for marine and steel structures. Suited for ships, containers, port machinery and mine equipment. Available in standard (35µm) and high-build (60µm) DFT versions.
Overview
Single-pack chlorinated rubber topcoat with a tough, glossy film.
Provides weathering resistance, water resistance, seawater resistance, and chemical resistance.
Composition
Formulated with chlorinated rubber resin, quality pigments, plasticizer, thixotropic agent, solvents, and additives.
Typical uses
Topcoat for ships, containers, port machinery, mine equipment, gas holders, steel structure bridges, and concrete facilities.
Technical data (typical)
Appearance: Various colors.
Theoretical consumption: 0.16 kg/m² at 40 μm DFT (excluding loss).
Density: 1.2 kg/L.
Drying time (25°C): Surface dry 1 h; hard dry 12 h.
Application data (25°C)
Mixing: Single-pack.
Induction time: None.
Pot life: Unlimited.
Application methods: Airless spray, brush, roller.
Thinner: X-15 chlorinated rubber thinner; dilution 3–7%.
Recoat interval (25°C): Min 12 h; max unlimited.
Recommended coats / DFT: 1 coat 40–60 μm; brush/roller 1 coat 30–45 μm.
Surface preparation
Remove dust, oil, and debris from the previous coat; if beyond maximum recoat interval, consider roughening as needed.
When used as the first coat: blast/shot blast to Sa 2.5 or power-tool cleaning to St 3; surface profile 30–75 μm.
System compatibility / packing / storage
Compatibility: Previous coat—epoxy primer; epoxy intermediate coating; chlorinated rubber anti-rust coating.
Packing: 25 kg.
Storage: Shelf life 12 months; store dry/cool/ventilated, away from fire and direct sunlight; no outdoor stacking.
We would love to speak with you.
Feel free to reach out using the below details.
Single-component water-based intumescent coating with 2-hour fire rating and outstanding weathering resistance for exterior steel structures. Resistant to UV, salt spray, freeze-thaw and acid-alkali exposure. Sa2.5 prep, 1.7–3.2mm application thickness.
2K alkyl silicate inorganic zinc primer delivering cathodic protection with weld and cut tolerance on structural steel. Suited for low-temperature application with universal topcoat compatibility. Sa2.5 prep required, 30µm DFT.
2K epoxy zinc-rich primer engineered for cathodic protection on structural steel. Suited for shipbuilding, bridges & oil tanks in aggressive environments. Sa2.5 prep required, 35–40µm DFT.
Industrial anti-corrosion and protective coating manufacturer. Direct supply from factory — no agents. ISO 9001 certified. Exporting to 30+ countries.