2K cold-applied zinc-rich primer offering cathodic protection equivalent to thermal spray zinc for steel structures. Weld and cut tolerant with universal organic and inorganic topcoat compatibility. 25–30µm DFT, surface dry in 5 minutes.
Overview
Single-component cold galvanizing zinc-rich anti-rust anti-corrosion coating for steel structures, used as a primer where thermal spray zinc is not convenient.
Composition
Polyolefin resin, ultra-fine zinc powder, light-colored composite anti-rust pigments, additives, solvent.
Typical uses
Anti-corrosion primer for steel structures, especially where thermal spray zinc is not practical.
Technical data (typical)
Appearance: grey.
Theoretical consumption: 0.36 kg/m² at 50 µm DFT (loss not included).
Density: 3.0 kg/L.
Drying time (25°C): surface dry 10 min; hard dry 12 h; full cure 7 d.
Application data (25°C)
Mixing: single-component.
Induction time: none.
Pot life: unlimited.
Application methods: airless spray, brush.
Thinner: dedicated thinner, 3–9%.
Recoat interval: min 12 h; max unlimited.
Recommended DFT per coat: 60–80 µm (brush 40–50 µm).
Compatible topcoats: epoxy micaceous iron oxide intermediate coating, polyurethane topcoat, acrylic topcoat, etc.
Surface preparation
Steel: blast to Sa 2.5 or power-tool clean to St 3; surface profile 30–75 µm.
System compatibility / packing / storage
System compatibility: epoxy MIO intermediate coating, polyurethane topcoat, acrylic topcoat.
Packing: 30 kg.
Storage: dry, cool, ventilated; away from fire; avoid strong sunlight; no outdoor storage.
Shelf life: 6 months.
We would love to speak with you.
Feel free to reach out using the below details.
2K ethyl silicate inorganic zinc-rich primer with high zinc content for maximum cathodic protection on industrial steel. Engineered for bridges, transmission towers & oil pipelines. Weld and cut tolerant, Sa2.5 prep, 40–80µm DFT.
2K C6-modified epoxy MIO intermediate coat engineered to extend coating service life on marine and offshore structures. Pairs with epoxy zinc primer for layered cathodic and barrier protection. 50µm DFT, Sa2.5 prep.
2K epoxy MIO primer and intermediate coat with lamellar barrier structure for aggressive environments. Engineered for shipbuilding, bridges & port machinery. Single airless spray pass achieves 60–80µm DFT.