2K heat-resistant epoxy phenolic coating with outstanding water resistance, chemical resistance and high-temperature performance for marine and chemical service. Suited for storage tanks, pipelines and chemical process equipment. Ambient cure, Sa2.5 prep required.
Overview
Two-component heat-resistant epoxy phenolic coating with ambient-temperature curing.
Composition
Phenolic epoxy resin, pigments, solvent, additives; supplied as Part A & Part B.
Typical uses
Corrosion protection for facilities/equipment in seawater, groundwater, and fresh water service.
Also suitable for chemical equipment, pipelines, and tanks.
Technical data (typical)
Appearance: primer grey/iron red/reddish brown; topcoat black/medium grey, etc.
Theoretical consumption: 0.16 kg/m² at 60 µm DFT (loss not included).
Density: 1.4 kg/L.
Drying time (25°C): surface dry 1 h; hard dry 24 h; full cure 7 d.
Heat resistance: 250°C @ 4 h.
Application data (25°C)
Mixing ratio (A:B): 24:3.
Induction time: 5 min.
Pot life: 40 min.
Application methods: airless spray, brush, roller.
Thinner: X-7 epoxy thinner, 3–8%.
Recoat interval: min 24 h; max 7 d.
Recommended DFT per coat: 60–90 µm (brush 40–55 µm).
Surface preparation
Steel: blast to Sa 2.5 or power-tool clean to St 3; surface profile 30–75 µm.
System compatibility / packing / storage
System compatibility: PLFH-4 epoxy phenolic primer + epoxy phenolic topcoat.
Packing: Part A 24 kg; Part B 3 kg.
Storage: dry, cool, ventilated; away from fire; avoid strong sunlight; no outdoor storage.
Shelf life: 12 months.
We would love to speak with you.
Feel free to reach out using the below details.
2K modified epoxy iron oxide primer with enhanced water resistance and corrosion protection for steel and concrete. Compatible with polyurethane, acrylic & chlorinated rubber topcoats. Abrasion-resistant film, high adhesion, 35–40µm DFT.
2K epoxy glass flake coating with exceptional chemical resistance and abrasion resistance for severe corrosive environments. Engineered for offshore structures, chemical plants & wastewater facilities. Achieves up to 300µm DFT in heavy-duty applications.
2K epoxy MIO primer and intermediate coat with lamellar barrier structure for aggressive environments. Engineered for shipbuilding, bridges & port machinery. Single airless spray pass achieves 60–80µm DFT.