Aliphatic polyurethane premium topcoat (2K) for durable finishing with weathering resistance.
For bridges, towers, vehicles, marine and port facilities.
Recoat interval: min 12 h, max 7 d.
Compatible over polyurethane or epoxy intermediate coatings.
Overview
Two-component aliphatic polyurethane premium topcoat for long-term protection and high-grade finishing on steel structures.
Provides resistance to chemical media corrosion, seawater, boiling water, oil, benzene solvents, and salt spray; designed for weathering and color retention.
Composition
Based on premium polyurethane resin, premium weather-resistant pigments, weathering extenders, solvents, and imported additives.
Cured with biuret; supplied in Part A & Part B packs.
Typical uses
For long-term protection and high-grade finishing on steel structures in various environments.
Typical applications include vehicles, bridges, steel towers, TV towers, construction machinery, marine and port facilities.
Technical data (typical)
Appearance: Various colors; high gloss, gloss, and matt.
Theoretical consumption: 0.11 kg/m² at 35 μm (excluding loss).
Density: 1.2 kg/L.
Drying time (25°C): Surface dry 1 h; hard dry 12 h; fully cured 7 d.
Adhesion: Grade 1; bending 1 mm; impact 50 kg·cm.
Application data (25°C)
Mixing ratio (Part A:Part B): 18:3.
Induction time: 5 min.
Pot life: 3 h.
Application methods: Airless spray, brush, roller.
Thinner: X-7 polyurethane thinner; dilution 3–7%.
Recoat interval (25°C): Min 12 h; max 7 d.
Recommended coats / DFT: 1 coat 35–50 μm; brush/roller 1 coat 30–40 μm.
Surface preparation
Remove dust and oil contamination from the previous coat; if beyond maximum recoat interval, roughen the surface.
When used as the first coat: blast/shot blast to Sa 2.5 or power-tool cleaning to St 3; surface profile 30–75 μm.
System compatibility / packing / storage
Compatibility: Previous coat—polyurethane intermediate coating; epoxy intermediate coating.
Packing: Part A 18 kg; Part B 3 kg.
Storage: Shelf life 12 months; store dry/cool/ventilated, away from fire and direct sunlight; no outdoor stacking.
We would love to speak with you.
Feel free to reach out using the below details.
Outdoor Intumescent Fireproof Coating for Steel Structure – Waterborne intumescent coating for outdoor steel fire protection.
2 h rating: ≥3.2 mm; 4.5 kg/m² theoretical consumption.
Air spray 0.6–0.8 MPa; nozzle Φ4.0–6.0 mm.
Bond strength test result: 0.77 MPa.
Inorganic Zinc Silicate Primer (2K) – Two-component inorganic zinc silicate primer for long-term steel corrosion protection with cathodic protection.
For blast-cleaned steel; surface preparation Sa 3 (not lower than Sa 2.5) is specified.
Fast drying at 25°C, RH 70–85%: touch dry 10 min; hard dry 2 h; cured 24 h.
Mix ratio 28:7; thinner X-11 inorganic zinc thinner (5–20%); compatible with epoxy/PU coating systems.
Modified Epoxy Iron Oxide Red Primer (2K) – Two-component modified epoxy iron oxide red anti-rust primer for steel and concrete.
For corrosion protection of steel structures and concrete surfaces.
Water and corrosion resistance with strong adhesion (as described).
Mix ratio 24:3; recoat 24 h–7 d (25°C).
Epoxy MIO intermediate coating (2K) for barrier protection in cathodic-protection coating systems.
Used with PLH53-35 epoxy zinc primer as a supporting intermediate coat.
Salt water resistance: 20 days (as stated).
Mixing ratio 8:1 (by weight); recommended DFT 60–90 µm per coat.