Single-component water-based alkyd enamel with tough film, strong adhesion and corrosion resistance for indoor and outdoor metal and wood structures. Non-flammable, low-VOC formulation. Sa2.5 prep, 50µm DFT per coat.
Overview
Waterborne alkyd general-purpose coating for interior and exterior metal and wood where basic corrosion protection and decorative hardness are required.
Film emphasizes hardness and adhesion with balanced mechanical properties and system compatibility for primer/topcoat use.
Composition
Waterborne alkyd resin as main binder with pigments, fillers, and special additives; single-component waterborne system using water as thinner.
Typical uses
General protective and decorative coating for indoor and outdoor metal and wood components, providing basic corrosion protection and appearance.
Technical data (typical)
Appearance: various colors.
Density: 1.25 kg/L.
Theoretical consumption: 0.15 kg/m² at 50 µm DFT (loss not included).
Drying time (25℃): surface dry 2 h; hard dry 24 h; full cure 7 d.
Forced drying (optional): flash-off 15 min, 90℃ for 15 min.
Application data (25°C)
Application methods: spray, brush, roller.
Thinner: pure water, ≤10%.
Recoat interval: ≥24 h.
Surface preparation
Steel: blast or power-tool clean to Sa 2.5 or St 3 with 30–75 µm profile before coating.
System compatibility / packing / storage
System compatibility: can be used in compatible waterborne alkyd systems on metal and wood substrates.
Storage: dry, cool, ventilated warehouse; 5–35℃; avoid strong sunlight, severe cold, and rain; keep containers sealed.
Shelf life: 6 months.
We would love to speak with you.
Feel free to reach out using the below details.
2K high-build epoxy topcoat with high-solids formulation for heavy-duty corrosion protection on steel and concrete. Outstanding chemical, solvent and water resistance. 60µm DFT per coat, 2-coat system to 120µm.
Cementitious hydrocarbon fire-resistant coating engineered for petrochemical and oil refining facilities exposed to hydrocarbon flame. Impact-resistant and crack-resistant with outstanding weathering performance. Sa2.5 prep, 24–33mm total application thickness.
Single-component water-based intumescent coating with 2-hour fire rating and outstanding weathering resistance for exterior steel structures. Resistant to UV, salt spray, freeze-thaw and acid-alkali exposure. Sa2.5 prep, 1.7–3.2mm application thickness.
Industrial anti-corrosion and protective coating manufacturer. Direct supply from factory — no agents. ISO 9001 certified. Exporting to 30+ countries.