2K silicone high-temperature coating system rated to 250°C/300°C with cathodic protection primer and weather-resistant topcoat for steel chimneys and industrial structures. Weld and cut tolerant, fast-drying. Sa2.5 prep, 50µm DFT primer.
Overview
Two-component silicone high-temperature anti-corrosion coating system supplied as primer and topcoat.
Composition
Alkyl silicate, silicone resin, functional pigments, heat-resistant pigments, anti-corrosion additives, curing agent; supplied as primer and topcoat.
Typical uses
High-temperature protection and marking coating for steel chimneys and other steel structures.
Technical data (typical)
Appearance: primer grey or iron red; topcoat white, silver white, black, green, etc.
Theoretical consumption: primer 0.11 kg/m² at 30 µm DFT (loss not included).
Theoretical consumption: topcoat 0.12 kg/m² at 30 µm DFT (loss not included).
Density: primer 1.4 kg/L; topcoat 1.2 kg/L.
Drying time (25°C): surface dry 1 h; hard dry 24 h; full cure 7 d.
Application data (25°C)
Mixing ratio (A:B): primer 25:0.5.
Mixing ratio (A:B): topcoat 20:0.4.
Induction time: none.
Pot life: 6 h.
Application methods: airless spray, brush.
Thinner: W61 dedicated thinner, 5–9%.
Recoat interval: min 24 h; max unlimited.
Recommended DFT per coat: 20–30 µm.
Surface preparation
Steel: blast to Sa 2.5 or power-tool clean to St 3; surface profile 30–75 µm.
System compatibility / packing / storage
System compatibility: W61-250/300 silicone high-temperature anti-corrosion primer + topcoat.
Packing: primer Part A 25 kg, Part B 0.5 kg; topcoat Part A 20 kg, Part B 0.4 kg.
Storage: dry, cool, ventilated; away from fire; avoid strong sunlight; no outdoor storage.
Shelf life: 6 months.
We would love to speak with you.
Feel free to reach out using the below details.
Single-component water-based intumescent coating delivering a 2-hour fire rating for indoor steel structures and building frames. Non-toxic, low-VOC formulation with strong adhesion. Sa2.5 prep required, 1.7–3.3mm application thickness.
2K epoxy anti-corrosive primer that chemically reacts with surface corrosion to form a stable protective complex. Applies directly to corroded steel up to 60µm, minimizing surface preparation. Minimum 40µm DFT, universal topcoat compatibility.
Single-component epoxy ester primer engineered for anti-corrosive protection on ferrous metals. Suited for coastal and high-humidity industrial environments. Air-dry or low-temperature bake cure, 25–30µm DFT per coat.