Single-component cyanoacrylate penetrating waterproofing coating with low viscosity and outstanding anti-corrosive and anti-mold performance for concrete structures. Suited for cooling towers, wastewater pools and underground facilities. 30µm DFT, 120µm+ total system.
Overview
Single-component cyanate waterproof coating for waterproofing and damp-proofing on building structures.
Composition
Cyanate prepolymer, adhesion promoter, pigments, sealing additive, solvent, catalyst.
Typical uses
Waterproofing and damp-proofing for cooling tower internal walls, sewage tanks, and basements.
Can be used in systems with epoxy and polyurethane coatings.
Technical data (typical)
Appearance: brown.
Theoretical consumption: 0.16 kg/m² at 50 µm DFT (loss not included).
Density: topcoat 1.27 kg/L.
Drying time (25°C): surface dry 1 h; hard dry 24 h; full cure 7 d.
Application data (25°C)
Mixing: single-component.
Induction time: none.
Pot life: unlimited.
Application methods: airless spray, brush, roller.
Thinner: cyanate thinner, 3–7%.
Recoat interval: min 12 h; max 7 d.
Recommended DFT per coat: 40–60 µm (brush/roller 30–40 µm).
Surface preparation
Steel: blast to Sa 2.5 or power-tool clean to St 3; surface profile 30–75 µm.
Concrete: sound and dry; moisture content ≤6%; clean and free of oil/dirt; repair defects before coating.
System compatibility / packing / storage
System compatibility: cyanate waterproof primer + cyanate waterproof topcoat.
Packing: 25 kg.
Storage: dry, cool, ventilated; away from fire; avoid strong sunlight; no outdoor storage.
Shelf life: 12 months.
We would love to speak with you.
Feel free to reach out using the below details.
Single-component water-based intumescent coating with 2-hour fire rating and outstanding weathering resistance for exterior steel structures. Resistant to UV, salt spray, freeze-thaw and acid-alkali exposure. Sa2.5 prep, 1.7–3.2mm application thickness.
2K ethyl silicate inorganic zinc-rich primer with high zinc content for maximum cathodic protection on industrial steel. Engineered for bridges, transmission towers & oil pipelines. Weld and cut tolerant, Sa2.5 prep, 40–80µm DFT.
2K epoxy glass flake coating with exceptional chemical resistance and abrasion resistance for severe corrosive environments. Engineered for offshore structures, chemical plants & wastewater facilities. Achieves up to 300µm DFT in heavy-duty applications.
Industrial anti-corrosion and protective coating manufacturer. Direct supply from factory — no agents. ISO 9001 certified. Exporting to 30+ countries.