Single-component chlorinated rubber deck coating with anti-slip aggregate, abrasion resistance and oil and water resistance for ship deck protection. UV-stable, tenacious film adhesion. Surface dry in 1 hour, 50µm DFT per coat.
Overview
Chlorinated rubber deck coating for steel and wood deck surfaces requiring abrasion resistance and slip resistance.
Film emphasizes wear resistance, water resistance, oil resistance, and weathering performance with secure adhesion for ship deck applications.
Composition
Chlorinated rubber resin with modified alkyd resin, premium pigments, toughening agent, solvent, and additives.
Typical uses
Protection and slip-resistant coating for ship decks.
Technical data (typical)
Appearance: various colors.
Theoretical consumption: 0.14 kg/m² at 40 µm DFT (loss not included).
Density: 1.3 kg/L.
Drying time (25℃): surface dry 1 h; hard dry 24 h; full cure 7 d.
Application data (25°C)
Mixing ratio: single-pack.
Induction time: none.
Pot life: unlimited.
Application methods: airless spray, brush, roller.
Thinner: 101 thinner, 3–8%.
Recoat interval: min 8 h; max unlimited.
Recommended coats/DFT: 1 coat 35–50 µm; brush/roller 1 coat 30–40 µm.
Recommended undercoats: epoxy primer; chlorinated rubber antirust coating; chlorinated rubber intermediate coating.
Surface preparation
Over existing coating: remove dust, oil, and debris; roughen as needed if maximum recoat interval is exceeded.
As first coat: blast-clean steel to Sa 2.5 or power-tool clean to St 3; surface profile 30–75 µm.
System compatibility / packing / storage
Compatibility: compatible over epoxy primer and chlorinated rubber systems; suitable for low-temperature application; apply at RH ≤85%, avoid rain/snow/strong wind (>6.7 m/s)/heavy fog/intense sunlight.
Packing: 20 kg.
Storage: store in a dry, cool, ventilated warehouse; keep away from fire sources; avoid strong sunlight; no outdoor stacking; shelf life 12 months.
We would love to speak with you.
Feel free to reach out using the below details.
Cementitious non-intumescent fire-resistant coating with 3-hour fire rating and weather resistance for outdoor steel structures. Suited for stations, ports, warehouses and stadiums in aggressive environments. Sa2.5 prep, 16–33mm total application thickness.
2K alkyl silicate inorganic zinc primer delivering cathodic protection with weld and cut tolerance on structural steel. Suited for low-temperature application with universal topcoat compatibility. Sa2.5 prep required, 30µm DFT.
2K epoxy zinc phosphate primer with outstanding saltwater resistance and adhesion for heavy industrial applications. Engineered for port facilities, mining equipment & hydraulic steel in aggressive environments. Sa2.5 prep required, iron red or gray finish.
Industrial anti-corrosion and protective coating manufacturer. Direct supply from factory — no agents. ISO 9001 certified. Exporting to 30+ countries.