Single-component vinyl chloride ether anti-corrosive coating with excellent weathering, seawater and chemical resistance for ships, containers, port machinery and steel bridges. Low-temperature cure, fast-drying. 35µm DFT per coat.
Overview
Single-pack chlorinated ether anti-corrosion coating system supplied as primer and topcoat.
Composition
Chlorinated ether resin, pigments, plasticizer, thixotropic agent, surface additives, solvent.
Typical uses
Anti-corrosion for ships, containers, port machinery, mine equipment, gas holders, steel structure bridges, and steel/concrete facilities and equipment.
Technical data (typical)
Appearance: various colors.
Theoretical consumption: primer 0.17 kg/m² at 50 µm DFT (loss not included).
Theoretical consumption: topcoat 0.2 kg/m² at 50 µm DFT (loss not included).
Density: primer 1.4 kg/L; topcoat 1.25 kg/L.
Drying time (25°C): surface dry 1 h; hard dry 8 h; full cure 7 d.
Application data (25°C)
Mixing: single-pack.
Induction time: none.
Pot life: unlimited.
Application methods: airless spray, brush, roller.
Thinner: dedicated thinner, 3–8%.
Recoat interval: min 12 h; max unlimited.
Recommended DFT per coat: 30–50 µm (brush/roller 30–40 µm).
System: chlorinated ether primer + chlorinated ether topcoat.
Surface preparation
Steel: blast to Sa 2.5 or power-tool clean to St 3; surface profile 30–75 µm.
System compatibility / packing / storage
System compatibility: chlorinated ether primer + chlorinated ether topcoat.
Packing: 20 kg.
Storage: dry, cool, ventilated; away from fire; avoid strong sunlight; no outdoor storage.
Shelf life: 12 months.
We would love to speak with you.
Feel free to reach out using the below details.
Cementitious hydrocarbon fire-resistant coating engineered for petrochemical and oil refining facilities exposed to hydrocarbon flame. Impact-resistant and crack-resistant with outstanding weathering performance. Sa2.5 prep, 24–33mm total application thickness.
Single-component water-based intumescent coating delivering a 2-hour fire rating for indoor steel structures and building frames. Non-toxic, low-VOC formulation with strong adhesion. Sa2.5 prep required, 1.7–3.3mm application thickness.
2K epoxy iron oxide primer with impact-resistant film and strong adhesion on steel and concrete. Compatible with polyurethane, alkyd & chlorinated rubber topcoat systems. Ambient cure at 25°C, 35–40µm DFT.