2K epoxy phenolic coating with excellent resistance to acid, alkali, salt and chemical media for steel tanks and structures with elevated temperature requirements. Sa2.5 prep, 50µm DFT per coat, full cure in 10 days.
Overview
Two-component epoxy phenolic coating for chemical and seawater exposure.
Composition
Imported epoxy phenolic resin with curing agent, corrosion-resistant pigments, solvent, additives; supplied as Part A & Part B.
Typical uses
For steel structures, storage tanks, and equipment containing chemical media.
Technical data (typical)
Appearance: various colors.
Theoretical consumption: 0.14 kg/m² at 50 µm DFT (loss not included).
Density: 1.4 kg/L.
Drying time (25°C): surface dry 1 h; hard dry 24 h; full cure 7 d.
Application data (25°C)
Mixing ratio (A:B): 24:3.
Induction time: 5 min.
Pot life: 3 h.
Application methods: airless spray, brush, roller.
Thinner: dedicated thinner, 3–8%.
Recoat interval: min 24 h; max 7 d.
Recommended DFT per coat: 60–90 µm (brush/roller 40–50 µm).
System: epoxy phenolic primer + epoxy phenolic topcoat.
Surface preparation
Steel: blast to Sa 2.5 or power-tool clean to St 3; surface profile 30–75 µm.
System compatibility / packing / storage
System compatibility: epoxy phenolic primer + epoxy phenolic topcoat.
Packing: Part A 24 kg; Part B 3 kg.
Storage: dry, cool, ventilated; away from fire; avoid strong sunlight; no outdoor storage.
Shelf life: 12 months.
We would love to speak with you.
Feel free to reach out using the below details.
2K high-build epoxy topcoat with high-solids formulation for heavy-duty corrosion protection on steel and concrete. Outstanding chemical, solvent and water resistance. 60µm DFT per coat, 2-coat system to 120µm.
Single-component water-based intumescent coating delivering a 2-hour fire rating for indoor steel structures and building frames. Non-toxic, low-VOC formulation with strong adhesion. Sa2.5 prep required, 1.7–3.3mm application thickness.
2K alkyl silicate inorganic zinc primer delivering cathodic protection with weld and cut tolerance on structural steel. Suited for low-temperature application with universal topcoat compatibility. Sa2.5 prep required, 30µm DFT.
Industrial anti-corrosion and protective coating manufacturer. Direct supply from factory — no agents. ISO 9001 certified. Exporting to 30+ countries.