Single-component acrylic marking coating with outstanding UV resistance, color retention and heat and cold resistance for chimneys and steel towers. Fast-drying with low-temperature cure capability. 35µm DFT per coat, 120µm+ system.
Overview
Single-component premium acrylic marking coating with outstanding weathering resistance.
Designed for heat resistance, cold resistance, gloss retention, and color retention; fast drying and suitable for low-temperature application.
Composition
Formulated with premium acrylic resin, quality pigments, plasticizer, solvents, and additives.
Typical uses
For marking and protection on concrete-structure chimneys in power plants, and for marking/protection on steel towers.
Technical data (typical)
Appearance: White; bright red, etc.
Theoretical consumption: 0.14 kg/m² at 35 μm DFT (excluding loss).
Density: 1.2 kg/L.
Drying time (25°C): Surface dry 1 h; hard dry 10 h.
Gloss: ≥80.
Application data (25°C)
Mixing: Single-component.
Induction time: None.
Pot life: Unlimited.
Application methods: Airless spray, brush, roller.
Thinner: X-14 acrylic thinner; dilution 3–7%.
Recoat interval (25°C): Min 12 h; max unlimited.
Recommended coats / DFT: 1 coat 40–50 μm; brush/roller 1 coat 30–40 μm.
Surface preparation
Steel: blast/shot blast to Sa 2.5 or power-tool cleaning to St 3; surface profile 30–75 μm.
Concrete: must be dry (moisture content ≤6%), free of oil/contamination; apply after a sealing primer; for old coatings, consider roughening and remove chalked/loose areas.
System compatibility / packing / storage
Packing: 20 kg.
Storage: Shelf life 12 months; store dry/cool/ventilated, away from fire and direct sunlight; no outdoor stacking.
We would love to speak with you.
Feel free to reach out using the below details.
2K epoxy enamel with a porcelain-smooth, abrasion-resistant film for decorative heavy-duty corrosion protection on steel and concrete. Chemical, oil and moisture resistant. 30µm DFT per coat, 3-coat system to 100µm.
Cementitious non-intumescent fire-resistant coating with 3-hour fire rating and weather resistance for outdoor steel structures. Suited for stations, ports, warehouses and stadiums in aggressive environments. Sa2.5 prep, 16–33mm total application thickness.
2K epoxy anti-corrosive primer that chemically reacts with surface corrosion to form a stable protective complex. Applies directly to corroded steel up to 60µm, minimizing surface preparation. Minimum 40µm DFT, universal topcoat compatibility.