Chlorosulfonated polyethylene topcoat for chemical-atmosphere steel and concrete protection.
For corrosive environments on steel and concrete.
Single-pack; min recoat 24 h at 25°C.
Thinner X-1; dilution 3–7%.
Overview
Single-component chlorosulfonated polyethylene topcoat with resistance to chemical media corrosion.
Provides water resistance, oil resistance, weather resistance, and salt spray resistance; suitable for low-temperature application.
Composition
Formulated with chlorosulfonated polyethylene resin, synthetic resin, pigments, additives, auxiliaries, and mixed solvents.
Typical uses
Anti-corrosion finishing for steel structures and concrete surfaces under chemical-atmosphere and corrosive environment conditions.
Technical data (typical)
Appearance: Various colors.
Theoretical consumption: 0.16 kg/m² at 40 μm DFT (excluding loss).
Density: 1.2 kg/L.
Drying time (25°C): Surface dry 1 h; hard dry 24 h.
Application data (25°C)
Mixing: Single-pack.
Induction time: None.
Pot life: Unlimited.
Application methods: Airless spray, brush, roller.
Thinner: X-1 chlorosulfonated polyethylene thinner; dilution 3–7%.
Recoat interval (25°C): Min 24 h; max unlimited.
Recommended coats / DFT: 1 coat 40–60 μm; brush/roller 1 coat 30–405 μm.
Surface preparation
Remove dust and oil contamination from the previous coat; if beyond maximum recoat interval, consider roughening as needed.
When used as the first coat: blast/shot blast to Sa 2.5 or power-tool cleaning to St 3; surface profile 30–75 μm.
System compatibility / packing / storage
Compatibility: Previous coat—epoxy primer; epoxy intermediate coating; chlorosulfonated polyethylene primer.
Packing: 22 kg.
Storage: Shelf life 12 months; store dry/cool/ventilated, away from fire and direct sunlight; no outdoor stacking.
We would love to speak with you.
Feel free to reach out using the below details.
Outdoor Non-Intumescent Fireproof Coating for Steel Structure – Outdoor non-intumescent fireproof coating for steel structures.
3 h rating: ≥33 mm; 20–22 kg/m²; 5–6 coats.
Bond strength test result: 0.11 MPa.
Fire test: 33 mm thickness; 5400 mm span; 3.00 h.
Outdoor Intumescent Fireproof Coating for Steel Structure – Waterborne intumescent coating for outdoor steel fire protection.
2 h rating: ≥3.2 mm; 4.5 kg/m² theoretical consumption.
Air spray 0.6–0.8 MPa; nozzle Φ4.0–6.0 mm.
Bond strength test result: 0.77 MPa.
Indoor Intumescent Fireproof Coating for Steel Structure – Waterborne intumescent coating for indoor steel fire protection.
2 h rating: ≥3.3 mm; 4.6 kg/m² theoretical consumption.
Water-thinnable; max dilution 5%.
Bond strength test result: 0.82 MPa.
Vinyl Phosphating Primer (2K) – Two-component phosphating primer for galvanized steel, aluminum, and other light metals.
Forms chemical adhesion to improve intercoat adhesion of subsequent coatings.
Low film thickness system: 15–25 µm DFT per coat; theoretical consumption 0.06 kg/m² at 20 µm DFT.
Min. recoat 2 h (25°C); dedicated PLX06 thinner (10–20%).
Protect. Perform. Endure. – Advanced Coatings for Industrial Excellence.
© 2025 All Rights reserved Anhui HUILI Coating Technology Co., Ltd. | Privacy Policy