2K water-based epoxy anti-static coating with excellent oil, water and corrosion resistance for crude oil, gasoline and diesel storage tank interiors. Low-VOC, non-flammable formulation. Sa2.5 prep, 40µm DFT per coat.
Overview
Two-component waterborne epoxy antistatic coating for steel tank internals where antistatic and anti-corrosion performance are both required.
Formulated for crude oil and refined fuel tanks, providing durable adhesion, chemical resistance, and conductive pathways for static dissipation.
Composition
Waterborne epoxy resin and curing agent with pigments, additives, and composite conductive materials; supplied as Part A & Part B; water as thinner.
Typical uses
Internal antistatic and anti-corrosion protection for compartments and storage tanks carrying crude oil, gasoline, kerosene, diesel, and similar media.
Technical data (typical)
Appearance: light grey.
Theoretical consumption: 0.11 kg/m² at 40 µm DFT (loss not included).
Drying time (25℃): surface dry 2 h; hard dry 24 h; full cure 7 d.
Application data (25°C)
Application methods: spray, brush, roller.
Pot life: 2 h at 25℃.
Thinner: clean water, 5–15%.
Recoat interval: min 24 h; max 7 d.
Surface preparation
Steel structures: blast-clean or power-tool clean to Sa 2.5 or St 3 with 30–75 µm surface profile.
System compatibility / packing / storage
System compatibility: used as internal lining over compatible primers or directly on properly prepared steel according to tank-lining specification.
Construction conditions: ambient 10–35℃ and at least 3℃ above dew point; not suitable in rain, fog, snow, or when RH ≥85%.
Storage: dry, cool, ventilated warehouse; 5–35℃; avoid exposure, severe cold, and rain.
Shelf life: 6 months.
We would love to speak with you.
Feel free to reach out using the below details.
2K ethyl silicate inorganic zinc-rich primer with high zinc content for maximum cathodic protection on industrial steel. Engineered for bridges, transmission towers & oil pipelines. Weld and cut tolerant, Sa2.5 prep, 40–80µm DFT.
Single-component epoxy ester primer engineered for anti-corrosive protection on ferrous metals. Suited for coastal and high-humidity industrial environments. Air-dry or low-temperature bake cure, 25–30µm DFT per coat.
2K C6-modified epoxy MIO intermediate coat engineered to extend coating service life on marine and offshore structures. Pairs with epoxy zinc primer for layered cathodic and barrier protection. 50µm DFT, Sa2.5 prep.