2K epoxy coal tar coating with seawater resistance, stray current resistance and anti-microbial performance. Engineered for buried pipelines and submerged tank floors. Sa2.5 prep, 60µm DFT per coat.
PLHL52-4 Epoxy Coal Tar Bitumen Anti-Corrosion Coating is a two-component epoxy coal tar bitumen anti-corrosion coating supplied as primer and topcoat. This coating is used for long-term anti-corrosion on external surfaces of buried pipelines, bottom plates of liquid storage tanks, and steel or concrete in submerged or wet-dry alternating environments.
It is composed of epoxy resin, coal tar pitch, anti-rust pigments, fillers, solvent, and additives, with a modified amine curing agent, and is supplied as Part A and Part B.
Supplied as primer and topcoat.
Designed for long-term anti-corrosion.
Suitable for external surfaces of buried pipelines.
Suitable for bottom plates of liquid storage tanks.
Suitable for steel and concrete in submerged environments.
Suitable for steel and concrete in wet-dry alternating environments.
This coating is suitable for a wide range of steel and concrete protection projects in industrial and buried service environments.
External surfaces of buried pipelines
Bottom plates of liquid storage tanks
Steel in submerged environments
Concrete in submerged environments
Steel in wet-dry alternating environments
Concrete in wet-dry alternating environments
Blast to Sa 2.5 or power-tool clean to St 3; surface profile 30–75 µm.
Storage
store in a dry, cool, ventilated place; keep away from fire; avoid strong sunlight; no outdoor storage.
System compatibility: (high-build) epoxy coal tar bitumen primer + (high-build) epoxy coal tar bitumen topcoat.
This product is a two-component epoxy coal tar bitumen anti-corrosion coating supplied as primer and topcoat.
This coating is used for long-term anti-corrosion on buried pipelines, tank bottom plates, and steel or concrete in submerged or wet-dry alternating environments.
Yes. This coating is used on steel and concrete in submerged or wet-dry alternating environments.
This coating can be applied by airless spray, brush, or roller.
The recommended dry film thickness per coat is 50–80 µm, or 35–50 µm by brush/roller.
System compatibility includes (high-build) epoxy coal tar bitumen primer and (high-build) epoxy coal tar bitumen topcoat.
We would love to speak with you.
Feel free to reach out using the below details.
Cementitious non-intumescent fire-resistant coating with 3-hour fire rating and weather resistance for outdoor steel structures. Suited for stations, ports, warehouses and stadiums in aggressive environments. Sa2.5 prep, 16–33mm total application thickness.
2K ethyl silicate inorganic zinc-rich primer with high zinc content for maximum cathodic protection on industrial steel. Engineered for bridges, transmission towers & oil pipelines. Weld and cut tolerant, Sa2.5 prep, 40–80µm DFT.
Single-component epoxy ester primer engineered for anti-corrosive protection on ferrous metals. Suited for coastal and high-humidity industrial environments. Air-dry or low-temperature bake cure, 25–30µm DFT per coat.
Industrial anti-corrosion and protective coating manufacturer. Direct supply from factory — no agents. ISO 9001 certified. Exporting to 30+ countries.