Single-component chlorinated rubber acrylic hull coating with outstanding UV resistance, seawater resistance and impact resistance for above-waterline ship hull surfaces. Flexible, tenacious film. Surface dry in 30 minutes, 45µm DFT per coat.
Overview
Chlorinated rubber acrylic hull coating for ship hull areas above the waterline where weatherability and seawater resistance are required.
Performance focus: toughness, impact resistance, decorative finish, and low-temperature application capability.
Composition
Chlorinated rubber resin with acrylic resin, special weather-resistant pigments, toughening agent, solvent, and additives.
Typical uses
Surface protection and decoration for ship hull exterior areas above the waterline.
Technical data (typical)
Appearance: various colors.
Theoretical consumption: 0.16 kg/m² at 40 µm DFT (loss not included).
Density: 1.2 kg/L.
Drying time (25℃): surface dry 1 h; hard dry 24 h; full cure 7 d.
Application data (25°C)
Mixing ratio: single-pack.
Induction time: none.
Pot life: unlimited.
Application methods: airless spray, brush, roller.
Thinner: 101 thinner, 3–8%.
Recoat interval: min 8 h; max unlimited.
Recommended coats/DFT: 1 coat 30–50 µm; brush/roller 1 coat 30–40 µm.
Recommended undercoats: epoxy primer; chlorinated rubber antirust coating; chlorinated rubber intermediate coating.
Surface preparation
Over existing coating: remove dust, oil, and debris; roughen as needed if maximum recoat interval is exceeded.
As first coat: blast-clean steel to Sa 2.5 or power-tool clean to St 3; surface profile 30–75 µm.
System compatibility / packing / storage
Compatibility: compatible over epoxy primer and chlorinated rubber systems; suitable for low-temperature application; apply at RH ≤85%, avoid rain/snow/strong wind (>6.7 m/s)/heavy fog/intense sunlight.
Packing: 20 kg.
Storage: store in a dry, cool, ventilated warehouse; keep away from fire sources; avoid strong sunlight; no outdoor stacking; shelf life 12 months.
We would love to speak with you.
Feel free to reach out using the below details.
Single-component water-based intumescent coating delivering a 2-hour fire rating for indoor steel structures and building frames. Non-toxic, low-VOC formulation with strong adhesion. Sa2.5 prep required, 1.7–3.3mm application thickness.
2K epoxy sealer primer engineered for deep penetration and encapsulation of concrete and cement substrates. Seals and stabilizes surfaces to optimize adhesion for subsequent coating systems. Surface dry in 1 hour, full cure in 7 days.
2K epoxy iron oxide primer with impact-resistant film and strong adhesion on steel and concrete. Compatible with polyurethane, alkyd & chlorinated rubber topcoat systems. Ambient cure at 25°C, 35–40µm DFT.
Industrial anti-corrosion and protective coating manufacturer. Direct supply from factory — no agents. ISO 9001 certified. Exporting to 30+ countries.