2K solvent-resistant anti-static coating with excellent electrical conductivity and corrosion resistance for methanol, toluene, xylene and solvent storage tanks. Suited for chemical tank interiors and petroleum pipelines. Sa2.5 prep, 240µm+ total DFT.
Overview
Two-component solvent-resistant antistatic anti-corrosion coating for flammable liquid storage and transfer facilities.
Composition
Special resin and curing agent, antistatic conductive fillers, imported additives; supplied as Part A & Part B.
Typical uses
Internal linings of petroleum product storage tanks and pipelines requiring static dissipation.
Especially for inner-wall corrosion protection of solvent tanks storing methanol, ethanol, crude benzene, toluene, xylene, butyl acetate, cyclohexanone, styrene, etc.
Technical data (typical)
Standard: GB/T 50393-2017.
Theoretical consumption: 0.15 kg/m² at 60 µm DFT (loss not included).
Density: 1.35 kg/L.
Drying time (25°C): surface dry 2 h; hard dry 24 h.
Technical data table
| Item | Index | Test method | |
|---|---|---|---|
| Appearance | Light grey, smooth and flat | Visual | |
| Surface resistivity (Ω) | 10⁸–10¹¹ | GB/T 1410-2006 | |
| Adhesion (MPa) | ≥8 | GB/T 5210-2006 | |
| Flexibility (mm) | 1 | GB/T 1731-1993 | |
| Impact resistance (cm) | 50 | GB/T 1732-1993 | |
| Hot water resistance, 90–100°C, 48 h | No blistering, rusting, peeling, cracking | GB/T 1733-1993 | |
| Oil resistance, 60±2°C, 720 h | No blistering, rusting, cracking, peeling | SY/T 0319-2021 | |
| Salt spray resistance, 1000 h, Grade 1 | No blistering, rusting, cracking, peeling | GB/T 1771-2007 | |
| 5% H₂SO₄, 720 h | No blistering, rusting, cracking, peeling | GB/T 9274-1988 | |
| 5% NaOH, 720 h | As tested | GB/T 9274-1988 | |
| 5% NaCl, 720 h | As tested | GB/T 9274-1988 | |
| Crude benzene, 60±2°C, 720 h | As tested | SY/T 0319-2021 | |
| Methanol, ambient, 90 d | As tested | SY/T 0319-2021 | |
| Anhydrous butyl acetate, ambient, 90 d | As tested | SY/T 0319-2021 | |
| Propylene glycol methyl ether, ambient, 90 d | As tested | SY/T 0319-2021 | |
| Cyclohexanone, ambient, 90 d | As tested | SY/T 0319-2021 | |
| Styrene, ambient, 90 d | As tested | SY/T 0319-2021 | |
Application data (25°C)
Mixing ratio (A:B): 24:2.
Induction time: 5 min.
Pot life: 2 h.
Application methods: airless spray, brush, roller.
Thinner: dedicated thinner, 3–8%.
Recoat interval: 24 h; max 7 d.
Recommended DFT per coat: 60–90 µm; total tank lining thickness 250–350 µm.
System: PLT-1 antistatic primer + intermediate + topcoat.
Surface preparation
Steel: blast to Sa 2.5 or power-tool clean to St 3; surface profile 30–75 µm.
System compatibility / packing / storage
System compatibility: PLT-1 antistatic primer + intermediate + topcoat.
Packing: Part A 24 kg; Part B 2 kg.
Storage: dry, cool, ventilated; away from fire; avoid strong sunlight; no outdoor storage.
Shelf life: 12 months.
We would love to speak with you.
Feel free to reach out using the below details.
2K epoxy enamel with a porcelain-smooth, abrasion-resistant film for decorative heavy-duty corrosion protection on steel and concrete. Chemical, oil and moisture resistant. 30µm DFT per coat, 3-coat system to 100µm.
2K epoxy zinc phosphate primer with outstanding saltwater resistance and adhesion for heavy industrial applications. Engineered for port facilities, mining equipment & hydraulic steel in aggressive environments. Sa2.5 prep required, iron red or gray finish.
2K C6-modified epoxy MIO intermediate coat engineered to extend coating service life on marine and offshore structures. Pairs with epoxy zinc primer for layered cathodic and barrier protection. 50µm DFT, Sa2.5 prep.
Industrial anti-corrosion and protective coating manufacturer. Direct supply from factory — no agents. ISO 9001 certified. Exporting to 30+ countries.