2K solvent-free anti-static epoxy coating with zero VOC and resistance to aviation fuel, diesel and lubricant oil for fuel storage tank interiors. Single coat achieves 150µm DFT. Sa2.5 prep, 300µm+ total system.
Overview
Two-component solvent-free conductive anti-static epoxy coating for internal linings of fuel tanks and compartments.
Composition
Low-viscosity epoxy resin, imported modified curing agent, conductive pigments, and additives; supplied as Part A & Part B.
Typical uses
Internal lining anti-corrosion for compartments and oil storage tanks handling gasoline, diesel, kerosene, and engine oil.
Technical data (typical)
Appearance: grey or light grey.
Theoretical consumption: 0.14 kg/m² at 100 µm DFT (loss not included).
Density: 1.4 kg/L.
Drying time (25°C): surface dry 1 h; hard dry 24 h; full cure 7 d.
Application data (25°C)
Mixing ratio (A:B): 20:5.
Induction time: 5 min.
Pot life: 50 min.
Application methods: airless spray, brush, roller.
Thinner: use none/minimal; if air pressure is insufficient, X-7 epoxy thinner may be used.
Recoat interval: min 12 h; max 7 d.
Recommended DFT per coat: 90–120 µm (brush 40–50 µm).
System compatibility: solvent-free conductive anti-static epoxy coating.
Surface preparation
Steel: blast to Sa 2.5 or power-tool clean to St 3; surface profile 30–75 µm.
System compatibility / packing / storage
Packing: Part A 20 kg; Part B 5 kg.
Storage: dry, cool, ventilated; away from fire; avoid strong sunlight; no outdoor storage.
Shelf life: 12 months.
We would love to speak with you.
Feel free to reach out using the below details.
2K alkyl silicate inorganic zinc primer delivering cathodic protection with weld and cut tolerance on structural steel. Suited for low-temperature application with universal topcoat compatibility. Sa2.5 prep required, 30µm DFT.
2K epoxy anti-corrosive primer that chemically reacts with surface corrosion to form a stable protective complex. Applies directly to corroded steel up to 60µm, minimizing surface preparation. Minimum 40µm DFT, universal topcoat compatibility.
2K epoxy iron oxide primer with impact-resistant film and strong adhesion on steel and concrete. Compatible with polyurethane, alkyd & chlorinated rubber topcoat systems. Ambient cure at 25°C, 35–40µm DFT.
Industrial anti-corrosion and protective coating manufacturer. Direct supply from factory — no agents. ISO 9001 certified. Exporting to 30+ countries.