Perchloroethylene enamel for mechanical equipment and metal parts finishing.
For protective and decorative finishing on metals.
Single-component; min recoat 12 h at 25°C.
Thinner X-1; dilution 3–7%.
Overview
Single-component perchloroethylene enamel with good gloss and flexibility.
Full-bodied film with corrosion resistance, weather resistance, water resistance, and oil resistance; suitable for low-temperature application.
Composition
Formulated with perchloroethylene resin, modified resin, quality pigments, extenders, plasticizer, and mixed solvents.
Typical uses
Protective and decorative finishing for various mechanical equipment and metal parts.
Technical data (typical)
Appearance: Various colors (gloss); also available in satin or matt.
Theoretical consumption: 0.16 kg/m² at 40 μm DFT (excluding loss).
Density: 1.2 kg/L.
Drying time (25°C): Surface dry 1 h; hard dry 24 h.
Application data (25°C)
Mixing: Single-component.
Induction time: None.
Pot life: Unlimited.
Application methods: Airless spray, brush, roller.
Thinner: X-1 thinner; dilution 3–7%.
Recoat interval (25°C): Min 12 h; max unlimited.
Recommended coats / DFT: 1 coat 40–60 μm; brush/roller 1 coat 30–40 μm.
Surface preparation
Steel: blast/shot blast to Sa 2.5, or power-tool cleaning to St 3.
Surface profile: 30–75 μm.
System compatibility / packing / storage
Compatibility: Previous coat—epoxy primer; epoxy intermediate coating; perchloroethylene anti-corrosion primer.
Packing: 20 kg.
Storage: Shelf life 12 months; store dry/cool/ventilated, away from fire and direct sunlight; no outdoor stacking.
We would love to speak with you.
Feel free to reach out using the below details.
High-Grade Epoxy Enamel (2K) – Epoxy enamel for decorative heavy-duty corrosion protection.
For steel structures and concrete surfaces.
Mix ratio 20:4; pot life 4 h.
Recoat 12 h–7 d; X-7 thinner 2–8%.
Indoor Intumescent Fireproof Coating for Steel Structure – Waterborne intumescent coating for indoor steel fire protection.
2 h rating: ≥3.3 mm; 4.6 kg/m² theoretical consumption.
Water-thinnable; max dilution 5%.
Bond strength test result: 0.82 MPa.
Inorganic Zinc Silicate Primer (2K) – Two-component inorganic zinc silicate primer for long-term steel corrosion protection with cathodic protection.
For blast-cleaned steel; surface preparation Sa 3 (not lower than Sa 2.5) is specified.
Fast drying at 25°C, RH 70–85%: touch dry 10 min; hard dry 2 h; cured 24 h.
Mix ratio 28:7; thinner X-11 inorganic zinc thinner (5–20%); compatible with epoxy/PU coating systems.
Epoxy zinc phosphate anti-rust primer (2K) for heavy-duty steel corrosion protection.
For ports/docks, heavy structures, mining machinery, power machinery plants, and water conservancy steelwork.
Zinc phosphate anti-rust pigment system with stated water and salt water resistance.
Mix ratio 7:1; theoretical consumption 0.12 kg/m² at 50 µm DFT.