PLX.52-1 High-chlorinated polyethylene enamel

Overview
Single-pack high-chlorinated polyethylene enamel with weathering resistance and color retention.​
Full-bodied film with bright color; resistant to chemical-atmosphere corrosion; fast drying and low-temperature applicable.​

Composition
Formulated with high-chlorinated polyethylene resin, chlorinated olefin resin, weather-resistant pigments, plasticizer, solvents, and additives.​

Typical uses
For anti-corrosion finishing on steel structures and concrete surfaces in chemical, petroleum, metallurgy, and power industries.​

Technical data (typical)

• Appearance: Various colors.​

• Theoretical consumption: 0.16 kg/m² at 40 μm DFT (excluding loss).​

• Density: 1.2 kg/L.​

• Drying time (25°C): Surface dry 1 h; hard dry 24 h.​

Application data (25°C)

• Mixing: Single-pack (silver white is split-pack; mixing ratio 6:1).​

• Induction time: None.​

• Pot life: Unlimited.​

• Application methods: Airless spray, brush, roller.​

• Thinner: X-16 high-chlorinated polyethylene thinner; dilution 3–7%.​

• Recoat interval (25°C): Min 12 h; max unlimited.​

• Recommended coats / DFT: 1 coat 40–60 μm; brush/roller 1 coat 30–45 μm.​

Surface preparation
Remove dust, oil, and debris from the previous coat; if beyond maximum recoat interval, consider roughening as needed.​
When used as the first coat: blast/shot blast to Sa 2.5 or power-tool cleaning to St 3; surface profile 30–75 μm.​

System compatibility / packing / storage

• Compatibility: Previous coat—epoxy intermediate coating; high-chlorinated polyethylene anti-rust coating; high-chlorinated polyethylene intermediate coating.​

• Packing: 22 kg.​

• Storage: Shelf life 12 months; store dry/cool/ventilated, away from fire and direct sunlight; no outdoor stacking.