Single-component chlorinated rubber acrylic topcoat retaining full chlorinated rubber corrosion resistance with improved gloss and weathering performance. Engineered for industrial facilities and steel structures in aggressive environments. Sa2.5 prep required.
Overview
Chlorinated rubber acrylic anti-corrosion topcoat for surface protection and finishing in harsh environments.
Provides anti-corrosion performance, a smooth/level film appearance, and improved weathering and gloss retention.
Composition
Formulated with chlorinated rubber modified acrylic resin, special pigments, solvents, and additives.
Typical uses
For surface anti-corrosion protection and finishing of equipment and industrial buildings/workshops in various harsh environments.
Technical data (typical)
Appearance: Various colors.
Density: 1.2 kg/L.
Theoretical consumption: 0.14 kg/m² at 35 μm DFT (excluding loss).
Drying time (25°C): Surface dry 1 h; hard dry 12 h.
Application data (25°C)
Mixing: Single-pack.
Induction time: None.
Pot life: Unlimited.
Application methods: Airless spray, brush, roller.
Thinner: Dedicated thinner; dilution 3–7%.
Recoat interval (25°C): Min 12 h; max unlimited.
Recommended coats / DFT: 1 coat 40–60 μm; brush/roller 1 coat 30–40 μm.
Surface preparation
Remove dust, oil, and debris from the previous coat; if beyond maximum recoat interval, consider roughening as needed.
When used as the first coat: blast/shot blast to Sa 2.5 or power-tool cleaning to St 3; surface profile 30–75 μm.
System compatibility / packing / storage
Compatibility: Previous coat—epoxy primer; epoxy intermediate coating; chlorinated rubber acrylic anti-rust primer; chlorinated rubber anti-rust primer.
Packing: 22 kg.
Storage: Shelf life 12 months; store in a dry, cool, ventilated place away from fire and direct sunlight; do not store outdoors.
We would love to speak with you.
Feel free to reach out using the below details.
Single-component water-based intumescent coating with 2-hour fire rating and outstanding weathering resistance for exterior steel structures. Resistant to UV, salt spray, freeze-thaw and acid-alkali exposure. Sa2.5 prep, 1.7–3.2mm application thickness.
2K modified epoxy iron oxide primer with enhanced water resistance and corrosion protection for steel and concrete. Compatible with polyurethane, acrylic & chlorinated rubber topcoats. Abrasion-resistant film, high adhesion, 35–40µm DFT.
2K epoxy MIO primer and intermediate coat with lamellar barrier structure for aggressive environments. Engineered for shipbuilding, bridges & port machinery. Single airless spray pass achieves 60–80µm DFT.
Industrial anti-corrosion and protective coating manufacturer. Direct supply from factory — no agents. ISO 9001 certified. Exporting to 30+ countries.