Single-component modified acrylic topcoat with enhanced corrosion resistance and weathering performance for steel and concrete structures. Suited for power generation, metallurgy, machinery and transportation industries. Ambient cure, 40µm DFT per coat.
Overview
Single-pack modified acrylic topcoat with good physical/mechanical properties and improved corrosion and weather resistance.
Suitable for low-temperature application.
Composition
Formulated with modified acrylic resin, solid acrylic resin, quality pigments, solvents, and additives.
Typical uses
Protective finishing for steel structures, concrete, and buildings in power, metallurgy, machinery, and transportation industries.
Technical data (typical)
Appearance: Various colors.
Theoretical consumption: 0.16 kg/m² at 40 μm DFT (excluding loss).
Density: 1.2 kg/L.
Drying time (25°C): Surface dry 0.5 h; hard dry 3 h.
Application data (25°C)
Mixing: Single-pack.
Induction time: None.
Pot life: Unlimited.
Application methods: Airless spray, brush, roller.
Thinner: X-14 acrylic thinner; dilution 3–7%.
Recoat interval (25°C): Min 12 h; max unlimited.
Recommended coats / DFT: 1 coat 40–60 μm; brush/roller 1 coat 30–40 μm.
Surface preparation
Remove dust and oil contamination from the previous coat; if beyond maximum recoat interval, consider roughening as needed.
When used as the first coat: blast/shot blast to Sa 2.5 or power-tool cleaning to St 3; surface profile 30–75 μm.
System compatibility / packing / storage
Compatibility: Previous coat—epoxy primer; epoxy micaceous iron oxide intermediate coating; chlorinated rubber anti-rust coating; acrylic anti-rust coating.
Packing: 22 kg.
Storage: Shelf life 12 months; store dry/cool/ventilated, away from fire and direct sunlight; no outdoor stacking.
We would love to speak with you.
Feel free to reach out using the below details.
Single-component water-based intumescent coating with 2-hour fire rating and outstanding weathering resistance for exterior steel structures. Resistant to UV, salt spray, freeze-thaw and acid-alkali exposure. Sa2.5 prep, 1.7–3.2mm application thickness.
Single-component water-based intumescent coating delivering a 2-hour fire rating for indoor steel structures and building frames. Non-toxic, low-VOC formulation with strong adhesion. Sa2.5 prep required, 1.7–3.3mm application thickness.
2K epoxy iron oxide primer with impact-resistant film and strong adhesion on steel and concrete. Compatible with polyurethane, alkyd & chlorinated rubber topcoat systems. Ambient cure at 25°C, 35–40µm DFT.