Epoxy coal tar bitumen anti-corrosion coating (2K) for buried pipelines and wet-dry service.
Buried pipelines, tank bottoms, submerged structures.
Mix ratio 7:1; recoat 12 h–7 d.
Resists seawater, salt spray, oil; anti-microbial.
PLHL52-4 Epoxy Coal Tar Bitumen Anti-Corrosion Coating is a two-component epoxy coal tar bitumen anti-corrosion coating supplied as primer and topcoat. This coating is used for long-term anti-corrosion on external surfaces of buried pipelines, bottom plates of liquid storage tanks, and steel or concrete in submerged or wet-dry alternating environments.
It is composed of epoxy resin, coal tar pitch, anti-rust pigments, fillers, solvent, and additives, with a modified amine curing agent, and is supplied as Part A and Part B.
Supplied as primer and topcoat.
Designed for long-term anti-corrosion.
Suitable for external surfaces of buried pipelines.
Suitable for bottom plates of liquid storage tanks.
Suitable for steel and concrete in submerged environments.
Suitable for steel and concrete in wet-dry alternating environments.
This coating is suitable for a wide range of steel and concrete protection projects in industrial and buried service environments.
External surfaces of buried pipelines
Bottom plates of liquid storage tanks
Steel in submerged environments
Concrete in submerged environments
Steel in wet-dry alternating environments
Concrete in wet-dry alternating environments
Blast to Sa 2.5 or power-tool clean to St 3; surface profile 30–75 µm.
Storage
store in a dry, cool, ventilated place; keep away from fire; avoid strong sunlight; no outdoor storage.
System compatibility: (high-build) epoxy coal tar bitumen primer + (high-build) epoxy coal tar bitumen topcoat.
This product is a two-component epoxy coal tar bitumen anti-corrosion coating supplied as primer and topcoat.
This coating is used for long-term anti-corrosion on buried pipelines, tank bottom plates, and steel or concrete in submerged or wet-dry alternating environments.
Yes. This coating is used on steel and concrete in submerged or wet-dry alternating environments.
This coating can be applied by airless spray, brush, or roller.
The recommended dry film thickness per coat is 50–80 µm, or 35–50 µm by brush/roller.
System compatibility includes (high-build) epoxy coal tar bitumen primer and (high-build) epoxy coal tar bitumen topcoat.
We would love to speak with you.
Feel free to reach out using the below details.
Epoxy Glass Flake Topcoat (2K) – Epoxy glass flake topcoat for wet or chemical zones.
For underwater/humid areas and heavy chemical plants.
Mix ratio 20:2; pot life 4 h.
Salt water resistance: 1 year, no change.
Epoxy Sealer Primer (2K) – Two-component penetrating sealer primer for porous substrates.
For cement mortar, concrete, and fiber cement boards; also stated for wood.
Concrete moisture content < 6% before application (as stated).
Mix ratio 16:4; theoretical consumption 0.29 kg/m² at 50 µm DFT.
Epoxy Red Lead Anti-Rust Primer (2K) – Two-component epoxy anti-rust primer for steel corrosion protection.
Epoxy Zinc Primer (2K, C6-Modified) – Two-component epoxy zinc primer (C6-modified) for cathodic-protection priming.
Salt spray resistance 1300 h (as stated).
Theoretical consumption 0.25 kg/m² at 50 µm DFT (losses not included).
For offshore platforms, underwater steel, pipelines, oil tanks, bridges, and petrochemical steel structures.