Epoxy ester anti-rust primer for steel structures (single-pack).
For guardrails and mining/mineshaft equipment steel surfaces.
Air-drying or low-temperature baking curing is specified.
Single-pack with no pot life limit (as stated); compatible with alkyd topcoats/enamels.
PLH53-4 Epoxy Ester Iron Oxide Red (Zinc Yellow) Anti-Rust Primer is a single-component epoxy ester anti-rust primer for steel structures; air-drying or low-temperature baking curing is specified.
The product is formulated with epoxy ester resin, iron oxide red, zinc oxide, corrosion inhibitor, extenders, additives, solvent, and drier. It is described as having good adhesion, a tough film, and convenient application for rust prevention.
Single-component anti-rust primer for steel structures
Specified for air-drying or low-temperature baking curing
Described as having good adhesion
Described as forming a tough film
Described as offering convenient application for rust prevention
Can be applied by airless spray, brush, or roller
This primer is suitable for steel corrosion protection projects in industrial environments.
Typical application areas
Steel structures
Guardrails
Mining equipment
Mineshaft equipment
Abrasive blasting or shot blasting to Sa 2.5, or power-tool cleaning to St 3; surface profile 30–75 µm.
Storage
Store in a dry, cool, ventilated warehouse away from fire sources and direct sunlight; outdoor storage is not permitted.
This primer is compatible with alkyd topcoat and alkyd enamel.
What is this primer used for?
This primer is used on steel structures for corrosion protection.
Is this a single-component product?
Yes. The product is supplied as a single-pack coating.
What curing method is specified?
Air-drying or low-temperature baking curing is specified.
What application methods are recommended?
The product can be applied by airless spray, brush, or roller.
What surface preparation is required before application?
Abrasive blasting or shot blasting to Sa 2.5, or power-tool cleaning to St 3, with a surface profile of 30–75 µm.
What topcoats are compatible with this primer?
It is compatible with alkyd topcoat and alkyd enamel.
We would love to speak with you.
Feel free to reach out using the below details.
Epoxy High-Build Topcoat (2K) – High-solids epoxy topcoat for heavy-duty protection.
For steel structures and concrete surfaces.
Induction time 5 h; pot life 3 h.
Recoat 24 h–7 d; X-7 thinner 3–9%.
Inorganic Zinc-Rich Primer (2K) – Two-component ethyl silicate zinc-rich primer for cathodic protection of blast-cleaned steel.
General-purpose use for bridges, towers, gas holders, oil tanks, oil/gas pipelines, and industrial steel structures.
High zinc dust content with stated water/oil/media resistance and welding/cutting resistance.
Sa 3 surface preparation (not lower than Sa 2.5); touch dry 10 min at 25°C, RH 70–85%.
Inorganic Zinc Silicate Primer (2K) – Two-component inorganic zinc silicate primer for long-term steel corrosion protection with cathodic protection.
For blast-cleaned steel; surface preparation Sa 3 (not lower than Sa 2.5) is specified.
Fast drying at 25°C, RH 70–85%: touch dry 10 min; hard dry 2 h; cured 24 h.
Mix ratio 28:7; thinner X-11 inorganic zinc thinner (5–20%); compatible with epoxy/PU coating systems.
Epoxy Zinc Primer (2K, C6-Modified) – Two-component epoxy zinc primer (C6-modified) for cathodic-protection priming.
Salt spray resistance 1300 h (as stated).
Theoretical consumption 0.25 kg/m² at 50 µm DFT (losses not included).
For offshore platforms, underwater steel, pipelines, oil tanks, bridges, and petrochemical steel structures.
Protect. Perform. Endure. – Advanced Coatings for Industrial Excellence.