Epoxy Red Lead Anti-Rust Primer (2K) – Two-component epoxy anti-rust primer for steel corrosion protection.
PLH53-1 Epoxy Red Lead Anti-Rust Primer is a two-component epoxy anti-rust primer for corrosion protection of steel structures and equipment.
The product is formulated with epoxy resin, red lead anti-rust pigment, fillers, additives, solvents, and an amine curing agent, and is supplied as Part A and Part B.
Designed for corrosion protection of steel structures and equipment
Suitable for use as an anti-corrosion primer on industrial steel surfaces
Can be applied by airless spray, brush, or roller
Suitable for gas holders, storage tanks, offshore platforms, and buried pipelines
Compatible with a wide range of intermediate coatings and topcoats
This primer is suitable for a wide range of steel protection projects in industrial and marine environments.
Typical application areas
Gas holders
Storage tanks
Mines
Offshore platforms
Underwater steel structures
Buried pipelines
Steel structures in factories and buildings
Equipment steel surfaces used as an anti-corrosion primer
Abrasive blasting or shot blasting to Sa 2.5, or power-tool cleaning to St 3. Surface profile: 30–75 µm.
Storage
Store in a dry, cool, ventilated warehouse away from fire sources and direct sunlight; outdoor storage is not permitted.
This primer is compatible with epoxy MIO intermediate coating, epoxy topcoat, polyurethane topcoat, acrylic topcoat, chlorinated rubber topcoat, high chlorinated polyethylene topcoat, chlorosulfonated polyethylene topcoat, and chlorinated ether topcoat.
What is this primer used for?
This primer is used for corrosion protection of steel structures and equipment.
What substrates and structures is it suitable for?
The product is suitable for gas holders, storage tanks, mines, offshore platforms, underwater steel structures, buried pipelines, steel structures in factories and buildings, and equipment steel surfaces.
What application methods are recommended?
The product can be applied by airless spray, brush, or roller.
What surface preparation is required before application?
Abrasive blasting or shot blasting to Sa 2.5 is recommended, or power-tool cleaning to St 3. A surface profile of 30–75 µm is specified.
What is the recommended recoat interval?
The minimum recoat interval is 24 h at 25°C, and the maximum interval is 7 days.
What coatings is it compatible with?
It is compatible with epoxy MIO intermediate coating, epoxy topcoat, polyurethane topcoat, acrylic topcoat, chlorinated rubber topcoat, high chlorinated polyethylene topcoat, chlorosulfonated polyethylene topcoat, and chlorinated ether topcoat.
We would love to speak with you.
Feel free to reach out using the below details.
Epoxy High-Build Topcoat (2K) – High-solids epoxy topcoat for heavy-duty protection.
For steel structures and concrete surfaces.
Induction time 5 h; pot life 3 h.
Recoat 24 h–7 d; X-7 thinner 3–9%.
High-Grade Epoxy Enamel (2K) – Epoxy enamel for decorative heavy-duty corrosion protection.
For steel structures and concrete surfaces.
Mix ratio 20:4; pot life 4 h.
Recoat 12 h–7 d; X-7 thinner 2–8%.
Vinyl Phosphating Primer (2K) – Two-component phosphating primer for galvanized steel, aluminum, and other light metals.
Forms chemical adhesion to improve intercoat adhesion of subsequent coatings.
Low film thickness system: 15–25 µm DFT per coat; theoretical consumption 0.06 kg/m² at 20 µm DFT.
Min. recoat 2 h (25°C); dedicated PLX06 thinner (10–20%).
Epoxy ester anti-rust primer for steel structures (single-pack).
For guardrails and mining/mineshaft equipment steel surfaces.
Air-drying or low-temperature baking curing is specified.
Single-pack with no pot life limit (as stated); compatible with alkyd topcoats/enamels.