Single-component water-based epoxy ester coating with strong adhesion and corrosion resistance for steel structures, bridges and chemical equipment. Non-flammable, low-VOC formulation suited for indoor metal decorative and protective applications. Sa2.5 prep, 50µm DFT per coat.
Overview
Waterborne epoxy ester coating for steel structures and equipment where anti-corrosion performance and adhesion are important.
Film focuses on good film formation and corrosion resistance with reliable adhesion to steel for industrial structures and indoor metalwork.
Composition
Waterborne epoxy ester resin as main binder with anti-rust pigments, functional fillers, and special waterborne additives; water as thinner.
Typical uses
Anti-corrosion and anti-rust protection for steel structures, metallurgy installations, bridges, and chemical equipment, as well as decorative protection for indoor metal facilities.
Technical data (typical)
Appearance: iron red or grey.
Density: 1.2 kg/L.
Theoretical consumption: 0.16 kg/m² at 50 µm DFT (loss not included).
Drying time (25℃): surface dry 3 h; hard dry 24 h; full cure 7 d.
Forced drying (optional): flash-off 15 min, 90℃ for 25 min.
Application data (25°C)
Application methods: spray, brush, roller.
Thinner: pure water, ≤10%.
Recoat interval: ≥24 h.
Surface preparation
Steel structures: blast or power-tool clean to Sa 2.5 or St 3 with 30–75 µm profile before coating.
System compatibility / packing / storage
System compatibility: used as part of waterborne epoxy ester anti-corrosion systems for steel in metallurgy, bridge, and chemical applications.
Construction conditions: ambient 5–35℃; not suitable in rain, fog, snow, or when RH ≥85%.
Storage: dry, cool, ventilated warehouse; 5–35℃; avoid strong sunlight, severe cold, and rain.
Shelf life: 6 months.
We would love to speak with you.
Feel free to reach out using the below details.
2K ethyl silicate inorganic zinc-rich primer with high zinc content for maximum cathodic protection on industrial steel. Engineered for bridges, transmission towers & oil pipelines. Weld and cut tolerant, Sa2.5 prep, 40–80µm DFT.
2K alkyl silicate inorganic zinc primer delivering cathodic protection with weld and cut tolerance on structural steel. Suited for low-temperature application with universal topcoat compatibility. Sa2.5 prep required, 30µm DFT.
2K epoxy anti-corrosive primer that chemically reacts with surface corrosion to form a stable protective complex. Applies directly to corroded steel up to 60µm, minimizing surface preparation. Minimum 40µm DFT, universal topcoat compatibility.