High-chlorinated polyethylene topcoat for steel and concrete anti-corrosion finishing.
For steel structures and concrete surfaces.
Single-pack; recoat 24 h to 7 d at 25°C.
Thinner X-16; dilution 3–7%.
Overview
Single-pack high-chlorinated polyethylene topcoat with chemical-atmosphere corrosion resistance and outdoor durability.
Full-bodied film, bright color, fast drying, suitable for low-temperature application.
Composition
Formulated with high-chlorinated polyethylene resin, modified resin, weather-resistant pigments, plasticizer, solvents, and additives.
Typical uses
Anti-corrosion finishing for steel structures and concrete surfaces.
Technical data (typical)
Appearance: Various colors.
Theoretical consumption: 0.16 kg/m² at 40 μm DFT (excluding loss).
Density: 1.2 kg/L.
Drying time (25°C): Surface dry 1 h; hard dry 24 h.
Application data (25°C)
Mixing: Single-pack.
Induction time: None.
Pot life: Unlimited.
Application methods: Airless spray, brush, roller.
Thinner: X-16 high-chlorinated polyethylene thinner; dilution 3–7%.
Recoat interval (25°C): Min 24 h; max 7 d.
Recommended coats / DFT: 1 coat 40–60 μm; brush/roller 1 coat 30–40 μm.
Surface preparation
Remove dust, oil, and debris from the previous coat; if beyond maximum recoat interval, consider roughening as needed.
When used as the first coat: blast/shot blast to Sa 2.5 or power-tool cleaning to St 3; surface profile 30–75 μm.
System compatibility / packing / storage
Compatibility: Previous coat—epoxy anti-rust coating; epoxy intermediate coating; high-chlorinated polyethylene anti-rust coating.
Packing: 22 kg.
Storage: Shelf life 12 months; store dry/cool/ventilated, away from fire and direct sunlight; no outdoor stacking.
We would love to speak with you.
Feel free to reach out using the below details.
Inorganic Zinc Silicate Primer (2K) – Two-component inorganic zinc silicate primer for long-term steel corrosion protection with cathodic protection.
For blast-cleaned steel; surface preparation Sa 3 (not lower than Sa 2.5) is specified.
Fast drying at 25°C, RH 70–85%: touch dry 10 min; hard dry 2 h; cured 24 h.
Mix ratio 28:7; thinner X-11 inorganic zinc thinner (5–20%); compatible with epoxy/PU coating systems.
Modified Epoxy Iron Oxide Red Primer (2K) – Two-component modified epoxy iron oxide red anti-rust primer for steel and concrete.
For corrosion protection of steel structures and concrete surfaces.
Water and corrosion resistance with strong adhesion (as described).
Mix ratio 24:3; recoat 24 h–7 d (25°C).
Epoxy zinc phosphate anti-rust primer (2K) for heavy-duty steel corrosion protection.
For ports/docks, heavy structures, mining machinery, power machinery plants, and water conservancy steelwork.
Zinc phosphate anti-rust pigment system with stated water and salt water resistance.
Mix ratio 7:1; theoretical consumption 0.12 kg/m² at 50 µm DFT.
Epoxy MIO Intermediate Coating (2K) – Two-component epoxy micaceous iron oxide intermediate coating for barrier protection.
For ships, containers, bridges, steel gates, gas holders, port machinery, and steel structures; used over zinc-rich primer or sprayed zinc.
Mix ratio 27:3; pot life 4 h (25°C).
Recoat 12 h–7 d (25°C); overcoatable with epoxy and polyurethane systems.
Protect. Perform. Endure. – Advanced Coatings for Industrial Excellence.
© 2025 All Rights reserved Anhui HUILI Coating Technology Co., Ltd. | Privacy Policy