Single-component water-based epoxy ester coating with strong adhesion and corrosion resistance for steel structures, bridges and chemical equipment. Non-flammable, low-VOC formulation suited for indoor metal decorative and protective applications. Sa2.5 prep, 50µm DFT per coat.
Overview
Waterborne epoxy ester coating for steel structures and equipment where anti-corrosion performance and adhesion are important.
Film focuses on good film formation and corrosion resistance with reliable adhesion to steel for industrial structures and indoor metalwork.
Composition
Waterborne epoxy ester resin as main binder with anti-rust pigments, functional fillers, and special waterborne additives; water as thinner.
Typical uses
Anti-corrosion and anti-rust protection for steel structures, metallurgy installations, bridges, and chemical equipment, as well as decorative protection for indoor metal facilities.
Technical data (typical)
Appearance: iron red or grey.
Density: 1.2 kg/L.
Theoretical consumption: 0.16 kg/m² at 50 µm DFT (loss not included).
Drying time (25℃): surface dry 3 h; hard dry 24 h; full cure 7 d.
Forced drying (optional): flash-off 15 min, 90℃ for 25 min.
Application data (25°C)
Application methods: spray, brush, roller.
Thinner: pure water, ≤10%.
Recoat interval: ≥24 h.
Surface preparation
Steel structures: blast or power-tool clean to Sa 2.5 or St 3 with 30–75 µm profile before coating.
System compatibility / packing / storage
System compatibility: used as part of waterborne epoxy ester anti-corrosion systems for steel in metallurgy, bridge, and chemical applications.
Construction conditions: ambient 5–35℃; not suitable in rain, fog, snow, or when RH ≥85%.
Storage: dry, cool, ventilated warehouse; 5–35℃; avoid strong sunlight, severe cold, and rain.
Shelf life: 6 months.
We would love to speak with you.
Feel free to reach out using the below details.
Cementitious non-intumescent fire-resistant coating with 3-hour fire rating for indoor steel structures including stations, warehouses and stadiums. Non-corrosive to steel, smoke-free and non-toxic. Sa2.5 prep, 16–32mm total application thickness.
Cementitious non-intumescent fire-resistant coating with 3-hour fire rating and weather resistance for outdoor steel structures. Suited for stations, ports, warehouses and stadiums in aggressive environments. Sa2.5 prep, 16–33mm total application thickness.
2K epoxy iron oxide primer with impact-resistant film and strong adhesion on steel and concrete. Compatible with polyurethane, alkyd & chlorinated rubber topcoat systems. Ambient cure at 25°C, 35–40µm DFT.