PLX52-2 High-chlorinated polyethylene topcoat

High-chlorinated polyethylene topcoat for steel and concrete anti-corrosion finishing.

For steel structures and concrete surfaces.
Single-pack; recoat 24 h to 7 d at 25°C.
Thinner X-16; dilution 3–7%.

HUILI anti-rust coatings metal paint pail

PLX52-2 High-chlorinated polyethylene topcoat Description

Overview
Single-pack high-chlorinated polyethylene topcoat with chemical-atmosphere corrosion resistance and outdoor durability.
Full-bodied film, bright color, fast drying, suitable for low-temperature application.

Composition
Formulated with high-chlorinated polyethylene resin, modified resin, weather-resistant pigments, plasticizer, solvents, and additives.

Typical uses
Anti-corrosion finishing for steel structures and concrete surfaces.

Technical data (typical)

Appearance: Various colors.
Theoretical consumption: 0.16 kg/m² at 40 μm DFT (excluding loss).
Density: 1.2 kg/L.
Drying time (25°C): Surface dry 1 h; hard dry 24 h.

Application data (25°C)

Mixing: Single-pack.
Induction time: None.
Pot life: Unlimited.
Application methods: Airless spray, brush, roller.
Thinner: X-16 high-chlorinated polyethylene thinner; dilution 3–7%.
Recoat interval (25°C): Min 24 h; max 7 d.
Recommended coats / DFT: 1 coat 40–60 μm; brush/roller 1 coat 30–40 μm.

Surface preparation
Remove dust, oil, and debris from the previous coat; if beyond maximum recoat interval, consider roughening as needed.
When used as the first coat: blast/shot blast to Sa 2.5 or power-tool cleaning to St 3; surface profile 30–75 μm.

System compatibility / packing / storage

Compatibility: Previous coat—epoxy anti-rust coating; epoxy intermediate coating; high-chlorinated polyethylene anti-rust coating.
Packing: 22 kg.
Storage: Shelf life 12 months; store dry/cool/ventilated, away from fire and direct sunlight; no outdoor stacking.

Contact Us

We would love to speak with you.
Feel free to reach out using the below details.

PLH52-3 Epoxy Glass Flake Topcoat

Epoxy Glass Flake Topcoat (2K) – Epoxy glass flake topcoat for wet or chemical zones.

For underwater/humid areas and heavy chemical plants.
Mix ratio 20:2; pot life 4 h.
Salt water resistance: 1 year, no change.

PLX06 Vinyl Phosphating Primer

Vinyl Phosphating Primer (2K) – Two-component phosphating primer for galvanized steel, aluminum, and other light metals.

Forms chemical adhesion to improve intercoat adhesion of subsequent coatings.
Low film thickness system: 15–25 µm DFT per coat; theoretical consumption 0.06 kg/m² at 20 µm DFT.
Min. recoat 2 h (25°C); dedicated PLX06 thinner (10–20%).

PLE06-3 Inorganic Zinc Silicate Primer

Inorganic Zinc Silicate Primer (2K) – Two-component inorganic zinc silicate primer for long-term steel corrosion protection with cathodic protection.

For blast-cleaned steel; surface preparation Sa 3 (not lower than Sa 2.5) is specified.
Fast drying at 25°C, RH 70–85%: touch dry 10 min; hard dry 2 h; cured 24 h.
Mix ratio 28:7; thinner X-11 inorganic zinc thinner (5–20%); compatible with epoxy/PU coating systems.

PLH53-7 Epoxy Glass Flake Anti-Rust Intermediate Coating

Epoxy Glass Flake Intermediate Coating (2K) – Two-component epoxy glass flake intermediate coating for heavy-duty barrier protection.

For marine/offshore, chemical areas, underground mines, and wastewater facilities; steel and concrete substrates.
Mix ratio 25:2.5; pot life 4 h (25°C).
Recoat 24 h–7 d (25°C); recommended DFT 60–80 µm per coat.